SABIC Innovative Plastics Lexan® FL2003 PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® FL2003 PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Various weight reductions at 0.250" (6.35mm) wall. Low temperature impact and high heat resistant. Excellent surface. UV-stabilized.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.09 g/cc
1.09 g/cc
foam molded; ASTM D 792
1.21 g/cc
1.21 g/cc
ASTM D 792
Water Absorption 0.13 %

@Time 86400 sec
0.13 %

@Time 24.0 hour
ASTM D 570
Moisture Absorption at Equilibrium 0.34 %

@Temperature 23.0 °C
0.34 %

@Temperature 73.4 °F
ASTM D 570
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Thickness 6.40 mm
0.0060 - 0.0080 in/in

@Thickness 0.252 in
SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength, Yield 53.0 MPa

@Thickness 6.35 mm
7690 psi

@Thickness 0.250 in
ASTM D 638
Elongation at Break 7.8 %

@Thickness 6.35 mm
7.8 %

@Thickness 0.250 in
ASTM D 638
Tensile Modulus 2.30 GPa

@Thickness 6.40 mm
334 ksi

@Thickness 0.252 in
ASTM D 638
Flexural Yield Strength 75.0 MPa

@Thickness 6.40 mm
10900 psi

@Thickness 0.252 in
ASTM D 790
Flexural Modulus 1.93 GPa

@Thickness 6.40 mm
280 ksi

@Thickness 0.252 in
ASTM D 790
Izod Impact, Unnotched 26.7 J/cm

@Temperature 23.0 °C
50.0 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Dart Drop, Total Energy 122 J

@Temperature 23.0 °C
90.0 ft-lb

@Temperature 73.4 °F
SABIC Method
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 55.8 µm/m-°C

@Temperature -40.0 - 95.0 °C
31.0 µin/in-°F

@Temperature -40.0 - 203 °F
ASTM E 831
Specific Heat Capacity 1.18 J/g-°C
0.282 BTU/lb-°F
ASTM C 351
Deflection Temperature at 0.46 MPa (66 psi) 137 °C

@Thickness 6.40 mm
279 °F

@Thickness 0.252 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 126 °C

@Thickness 6.40 mm
259 °F

@Thickness 0.252 in
unannealed; ASTM D 648
UL RTI, Electrical 80.0 °C
176 °F
UL 746B
UL RTI, Mechanical with Impact 80.0 °C
176 °F
UL 746B
UL RTI, Mechanical without Impact 80.0 °C
176 °F
UL 746B
Flammability, UL94 HB

@Thickness 5.99 mm
HB

@Thickness 0.236 in
UL 94
Oxygen Index 28.2 %
28.2 %
LOI; ASTM D 2863
Electrical Properties Metric English Comments
Volume Resistivity 3.60e+16 ohm-cm
3.60e+16 ohm-cm
ASTM D 257
Surface Resistance >= 1.10e+17 ohm
>= 1.10e+17 ohm
ASTM D 257
Dielectric Constant 2.47

@Frequency 100 Hz
2.47

@Frequency 100 Hz
ASTM D 150
2.68

@Frequency 1.00e+6 Hz
2.68

@Frequency 1.00e+6 Hz
ASTM D 150
Dissipation Factor 0.0037

@Frequency 100 Hz
0.0037

@Frequency 100 Hz
ASTM D 150
0.0039

@Frequency 1.00e+6 Hz
0.0039

@Frequency 1.00e+6 Hz
ASTM D 150
Descriptive Properties Value Comments
FOAM - ELECTRICAL 6.4 mm Wt Reduction, % 20
-
FOAM - Flame Class Minimum Density, g/cm^3 1.12
-
FOAM - IMPACT 6.4 mm Wt Reduction, % 10
-
FOAM - MECHANICAL 6.4 mm Wt Reduction, % 10
-
FOAM - PHYSICAL 6.4mm Wt Reduction, % 10
-
FOAM - THERMAL 6.4mm Wt Reduction, % 10
-
UV-light, water exposure/immersion F1
UL 746C