SABIC Innovative Plastics LNP THERMOCOMP DX06313 PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DX06313 PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polycarbonate base, 30% glass fiber reinforced, impact modified material. Thinwall housing, mobile phone. Some light color grades may have lower impact data than nature and black grade.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.42 g/cc | 1.42 g/cc | ASTM D792 |
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.100 % | 0.100 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.40 % | 0.40 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0050 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 4.6 g/10 min @Load 1.20 kg, Temperature 300 °C |
4.6 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| 42 g/10 min @Load 5.00 kg, Temperature 300 °C |
42 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 | |
| Melt Index of Compound | 32 g/10 min @Load 5.00 kg, Temperature 300 °C |
32 g/10 min @Load 11.0 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 90.0 MPa | 13100 psi | 5 mm/min; ISO 527 |
| 99.0 MPa | 14400 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 3.5 % | 3.5 % | 5 mm/min; ISO 527 |
| 3.6 % | 3.6 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 7.42 GPa | 1080 ksi | 1 mm/min; ISO 527 |
| 7.50 GPa | 1090 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 170 MPa | 24700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 170 MPa | 24700 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 6.65 GPa | 965 ksi | 2 mm/min; ISO 178 |
| 7.00 GPa | 1020 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.900 J/cm | 1.69 ft-lb/in | Light & White Colors; ASTM D256 |
| 1.90 J/cm | 3.56 ft-lb/in | Natural & Black Colors; ASTM D256 | |
| 1.20 J/cm @Temperature -30.0 °C |
2.25 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 16.0 kJ/m² | 7.61 ft-lb/in² | 80*10*4; ISO 180/1A |
| 12.0 kJ/m² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 24.0 J @Temperature 23.0 °C |
17.7 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 22.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
12.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 22.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
12.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 68.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 68.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
37.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 136 °C | 277 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 136 °C @Thickness 3.20 mm |
277 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 142 °C | 288 °F | Rate B/50; ASTM D1525 |
| 142 °C | 288 °F | Rate B/50; ISO 306 | |
| 143 °C | 289 °F | Rate B/120; ISO 306 |