Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 590 °F Product List

Thermal Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	310 °C	590 °F	ASTM D648
PBI Performance Products Celazole® TL-60 Self Lubricating Melt Processable Polybenzimidazole Celazole® polybenzimidazole (PBI) resin is a unique and highly stable linear hetrocyclic polymer. PBI is characterized by high strength; excellent thermal stability, and broad chemical resistance. ..
Deflection Temperature at 1.8 MPa (264 psi)	310 °C @Thickness 3.18 mm	590 °F @Thickness 0.125 in	Unannealed; ASTM D648
PolyOne Edgetek® PK-30GF/000 Polyetheretherketone (PEEK) The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for ..
Deflection Temperature at 1.8 MPa (264 psi)	310 °C	590 °F	Unannealed; ASTM D648
PolyOne Edgetek® PK-30GF/000 HT Polyaryletherketone, Glass Filled (discontinued **) Description/Features:30% Glass FilledPolyOne First ChoiceInformation provided by PolyOne Corporation.
Deflection Temperature at 1.8 MPa (264 psi)	310 °C	590 °F	ASTM D648
PBI Performance Products Celazole® TF-60 V Glass Fiber Reinforced Melt Processable Polybenzimidazole Celazole® polybenzimidazole (PBI) resin is a unique and highly stable linear hetrocyclic polymer. PBI is characterized by high strength; excellent thermal stability, and broad chemical resistance. ..
Deflection Temperature at 1.8 MPa (264 psi)	310 Â°C	590 Â°F	ASTM D648
Mitsui Arlenâ„¢ A335 35% Glass Fiber-Reinforced Modified Nylon 6T (COND) ARLENâ„¢ is a heat resistant, modified polyamide 6T developed by Mitsui Chemicals, Inc. With a high melting point (320Â°C) and a rigidity level comparable to super engineering plastics, it poss..
Deflection Temperature at 1.8 MPa (264 psi)	310 Â°C	590 Â°F	ASTM D648
Mitsui Arlenâ„¢ A335 35% Glass Fiber-Reinforced Modified Nylon 6T (DAM) ARLENâ„¢ is a heat resistant, modified polyamide 6T developed by Mitsui Chemicals, Inc. With a high melting point (320Â°C) and a rigidity level comparable to super engineering plastics, it poss..
Deflection Temperature at 1.8 MPa (264 psi)	310 Â°C	590 Â°F	ASTM D648
Mitsui Arlenâ„¢ A350 50% Glass Fiber-Reinforced Modified Nylon 6T (COND) ARLENâ„¢ is a heat resistant, modified polyamide 6T developed by Mitsui Chemicals, Inc. With a high melting point (320Â°C) and a rigidity level comparable to super engineering plastics, it poss..
Deflection Temperature at 1.8 MPa (264 psi)	310 Â°C	590 Â°F	ASTM D648
Mitsui Arlenâ„¢ A350 50% Glass Fiber-Reinforced Modified Nylon 6T (DAM) ARLENâ„¢ is a heat resistant, modified polyamide 6T developed by Mitsui Chemicals, Inc. With a high melting point (320Â°C) and a rigidity level comparable to super engineering plastics, it poss..
Deflection Temperature at 1.8 MPa (264 psi)	310 Â°C	590 Â°F	Unannealed; ISO 75-2/A
Solvay Specialty Polymers AmodelÂ® HFZ A-4133L Polyphthalamide (PPA), 33% Glass Fiber AmodelÂ® HFZ A-4133 L polyphthalamide (PPA) is a 33% glass-reinforced, hot water moldable resin. Key properties include heat resistance, reduced outgassing and high strength and stiffness over a b..
Deflection Temperature at 1.8 MPa (264 psi)	310 °C	590 °F	ASTM D648
E-Polymers SEPAZ® C230GP 30% Glass Fiber Reinforced LCP Resin Liquid Crystal Polymer Resin: SEPAZ LCP resin has a unique structure and performance unthought of in a traditional plastics. Beside SEPAZ LCP takes the excels in all-around performance and molding ..
Deflection Temperature at 1.8 MPa (264 psi)	310 °C	590 °F	ISO 75-1/-2
Barlog Plastics KEBAPEAK XC1730 PEEK; 30% carbon fiber reinforced PEEK-CF30Information provided by BARLOG plastics GmbH.
Deflection Temperature at 1.8 MPa (264 psi)	310 °C	590 °F	Unannealed; ISO 75-2/A
Solvay Specialty Polymers Amodel® HFZ A-4133L Polyphthalamide (PPA) (Unverified Data**) Amodel HFZ A-4133 L polyphthalamide (PPA) is a 33% glass-reinforced, hot water moldable resin. Key properties include heat resistance, reduced outgassing and high strength and stiffness over a broad..
Deflection Temperature at 1.8 MPa (264 psi)	310 °C	590 °F	Unannealed; ISO 75-2/A
Solvay Specialty Polymers Amodel® A-4133 L Polyphthalamide (PPA), Dry (discontinued **) Amodel A-4133L polyphthalamide (PPA) is a 33% glass reinforced resin designed to offer high crystallinity when molded in water-cooled molds. Key properties include high heat resistance, reduced outg..
Deflection Temperature at 1.8 MPa (264 psi)	310 °C @Thickness 3.20 mm	590 °F @Thickness 0.126 in	unannealed; ASTM D648
SABIC Innovative Plastics LNP STAT-KON LX00797C PEEK LNP* STAT-KON* LX00797C is a compound based on Polyetheretherketone containing Proprietary Filler(s). Added features of this material include: ristics of this grade are: Clean Compounding System, ..