SABIC Innovative Plastics LNP LUBRICOMP RL004S PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RL004S PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* RL004S is a compound based on Nylon 66 resin containing 20% PTFE. Added features of this material include: Heat Stabilized, Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ASTM D792 |
| 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.550 % | 0.550 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0188 - 0.0329 cm/cm @Time 86400 sec |
0.0188 - 0.0329 in/in @Time 24.0 hour |
ISO 294 |
| 0.019 - 0.033 cm/cm @Time 86400 sec |
0.019 - 0.033 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0188 - 0.0329 cm/cm @Time 86400 sec |
0.0188 - 0.0329 in/in @Time 24.0 hour |
ISO 294 |
| 0.019 - 0.033 cm/cm @Time 86400 sec |
0.019 - 0.033 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 55.0 MPa | 7980 psi | ISO 527 |
| 63.0 MPa | 9140 psi | ASTM D638 | |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | ISO 527 |
| 63.0 MPa | 9140 psi | ASTM D638 | |
| Elongation at Break | 6.2 % | 6.2 % | ASTM D638 |
| 7.2 % | 7.2 % | ISO 527 | |
| Elongation at Yield | 5.4 % | 5.4 % | ASTM D638 |
| 6.7 % | 6.7 % | ISO 527 | |
| Tensile Modulus | 2.48 GPa | 360 ksi | 50 mm/min; ASTM D638 |
| 2.60 GPa | 377 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 84.0 MPa | 12200 psi | ISO 178 |
| 88.0 MPa | 12800 psi | ASTM D790 | |
| Flexural Modulus | 2.27 GPa | 329 ksi | ASTM D790 |
| 2.40 GPa | 348 ksi | ISO 178 | |
| Izod Impact, Notched | 0.420 J/cm | 0.787 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.71 J/cm | 10.7 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 39.0 kJ/m² | 18.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 3.00 J | 2.21 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Coefficient of Friction, Dynamic | 0.32 | 0.32 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.21 | 0.21 | ASTM D3702 Modified |
| K (wear) Factor | 32.2 x 10-8 mm³/N-M | 16.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 97.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
54.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 79.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 70.0 °C @Thickness 3.20 mm |
158 °F @Thickness 0.126 in |
unannealed; ASTM D648 |