SABIC Innovative Plastics Cycoloy® RCY6113 PC+ABS (Asia Pacific)
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycoloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycoloy® RCY6113 PC+ABS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Cycoloy* RCY6113 resin is an injection moldable PC/ABS blend with non-brominated and non-chlorinated flame retardant. It contains 30% post consumer recycle content with a UL-94 5VB rating @ 2.0mm and V0 rating @ 1.5mm. Developed for wide variety of applications that require balanced flow and impact performance. Limited availability and restricted color only.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Water Absorption | 0.11 % @Time 86400 sec |
0.11 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0050 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0050 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 260 °C |
20 g/10 min @Load 4.76 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 47.0 MPa | 6820 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 60 % | 60 % | Type I, 50 mm/min; ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | Type I, 50 mm/min; ASTM D638 |
| Tensile Modulus | 2.50 GPa | 363 ksi | 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 90.0 MPa | 13100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.40 GPa | 348 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 5.00 J/cm | 9.37 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 55.0 kJ/m² | 26.2 ft-lb/in² | 80*10*3; ISO 180/1A |
| Dart Drop, Total Energy | 50.0 J @Temperature 23.0 °C |
36.9 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 71.0 µm/m-°C @Temperature -40.0 - 60.0 °C |
39.4 µin/in-°F @Temperature -40.0 - 140 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 76.0 µm/m-°C @Temperature -40.0 - 60.0 °C |
42.2 µin/in-°F @Temperature -40.0 - 140 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C @Thickness 6.40 mm |
194 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C @Thickness 3.20 mm |
167 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| 82.0 °C @Thickness 6.40 mm |
180 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 92.0 °C | 198 °F | Rate B/50; ASTM D1525 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
UL 94 |
| 5VB @Thickness 2.00 mm |
5VB @Thickness 0.0787 in |
UL 94 |