Polykemi AB SCANMID 6 B12^ F20 NH6 Nylon 6, Glass Fiber Reinforced, Halogen Free, Flame Retardant
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled , Nylon 6, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Polykemi AB |
| Trade Name | SCANMID 6 |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB SCANMID 6 B12^ F20 NH6 Nylon 6, Glass Fiber Reinforced, Halogen Free, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 |
| Filler Content | 20 % | 20 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | With Flow; ISO 2577 |
| 0.0090 cm/cm | 0.0090 in/in | Across Flow; ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 105 MPa | <= 15200 psi | ISO/R527 |
| Elongation at Break | 3.5 % | 3.5 % | ISO/R527 |
| Flexural Modulus | 6.40 GPa @Temperature 23.0 °C |
928 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 0.500 J/cm² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | >= 200 °C @Load 5.001 kg |
>= 392 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| Glow Wire Test | 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
IEC 695-2-1 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® HP6REU PC (Europe-Africa-Middle East)
- Arlon A3015-R004-12 0.015" (0.381 mm) Cured Fusible Silicone Rubber with Sinusoidal Fiberglass Substrate
- Imerys G-200 HP Feldspar
- Gouda Vuurvast VIBRON 170 M Dense Vibrating Refractory Castable
- Momentive Performance Materials Siloprenâ„¢ LSR 2841 Liquid Silicone Rubber - Good Flex Life
- Taiwan PU Corporation TPUI-H90 High Hydrolysis Resistance, Injection Molding Polyether Base TPU
- California Fine Wire Alloy 20-245 Precious Metal Alloy
- Asahi Kasei Thermylene® P6-16FG-0801 16% Fiber Glass Reinforced, UV Stabilized
- BASF Capron® HPN 9333G HS Impact Modified, 33% Glass-Filled Nylon 6 (Conditioned) (discontinued **)
Copyright © lookpolymers.com All Rights Reserved