Polykemi AB POLYshine PBT D211 PBT, Modified

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer Polykemi AB
Trade Name POLYshine
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polykemi AB POLYshine PBT D211 PBT, Modified.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 1.31 g/cc
0.0473 lb/in³
ISO 1183
Linear Mold Shrinkage 0.018 - 0.020 cm/cm
0.018 - 0.020 in/in
With Flow; ISO 2577
0.018 - 0.020 cm/cm
0.018 - 0.020 in/in
Across Flow; ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break <= 51.0 MPa
<= 7400 psi
ISO/R527
Elongation at Yield 8.0 %
8.0 %
ISO/R527
Flexural Strength <= 78.0 MPa
<= 11300 psi
ISO 178
Flexural Modulus 2.10 GPa

@Temperature 23.0 °C
 305 ksi

@Temperature 73.4 °F
 ISO 178
2.40 GPa

@Temperature -20.0 °C
 348 ksi

@Temperature -4.00 °F
 ISO 178
Charpy Impact Unnotched NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 ISO 179
NB

@Temperature -20.0 °C
 NB

@Temperature -4.00 °F
 ISO 179
Charpy Impact, Notched 0.500 J/cm²

@Temperature -20.0 °C
 2.38 ft-lb/in²

@Temperature -4.00 °F
 ISO 179
0.600 J/cm²

@Temperature 23.0 °C
 2.86 ft-lb/in²

@Temperature 73.4 °F
 ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 165 °C
329 °F
120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C
149 °F
120°C/h; ISO 75/1
Vicat Softening Point 175 °C

@Load 5.001 kg
 347 °F

@Load 11.03 lb
 50°C/h; ISO 306
212 °C

@Load 1.00 kg
 414 °F

@Load 2.21 lb
 50°C/h; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
Glow Wire Test 750 °C

@Thickness 2.00 mm
 1380 °F

@Thickness 0.0787 in
 IEC 695-2-1