PolyOne LubriOne™ NN-000/20T Polyamide 66 (Nylon 66)

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer PolyOne Corporation
Trade Name LubriOne™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne LubriOne™ NN-000/20T Polyamide 66 (Nylon 66).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. LubriOne compounds have been demonstrated to reduce friction, noise, vibration, heat buildup and improve product durability.Information provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.26 g/cc
1.26 g/cc
ASTM D792
Water Absorption 0.80 %

@Thickness 3.18 mm
0.80 %

@Thickness 0.125 in
@ 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.014 - 0.018 cm/cm
0.014 - 0.018 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Yield 65.5 MPa
9500 psi
Type I, 5.1 mm/min; ASTM D638
Elongation at Break 3.0 - 6.0 %
3.0 - 6.0 %
Type I, 5.1 mm/min; ASTM D638
Tensile Modulus 2.83 GPa
410 ksi
Type I, 5.1 mm/min; ASTM D638
Flexural Strength 107 MPa
15500 psi
ASTM D790
Flexural Modulus 2.83 GPa
410 ksi
ASTM D790
Izod Impact, Notched 0.430 J/cm

@Thickness 3.18 mm,
Temperature 23.0 °C
0.806 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
Injection Molded; ASTM D256A
Coefficient of Friction, Dynamic 0.41
0.41
vs. Steel - Dynamic; ASTM D1894
Coefficient of Friction, Static 0.23
0.23
vs. Steel - Static; ASTM D1894
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 232 °C

@Thickness 6.35 mm
450 °F

@Thickness 0.250 in
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 82.2 °C

@Thickness 6.35 mm
180 °F

@Thickness 0.250 in
Unannealed; ASTM D648
Processing Properties Metric English Comments
Melt Temperature 277 - 304 °C
531 - 579 °F
Descriptive Properties Value Comments
Features Good Wear Resistance
Low Friction
Lubricated
Forms Pellets
Generic Material Nylon 66
Generic Name Polyamide 66 (Nylon 66)
Processing Method Injection Molding
Regional Availability Africa & Middle East
Asia Pacific
Europe
South America
Uses Appliance Components
Automotive Applications
Bearings
Business Equipment
Consumer Applications
Conveyor Parts
Gears
Industrial Applications
Printer Parts
Pulleys
Rollers