SABIC Innovative Plastics GELOY FXW710SK ASA

Category Polymer , Thermoplastic , ASA Polymer
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name GELOY
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics GELOY FXW710SK ASA.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
General purpose injection molding ASA with Visual Fx sparkle effect.
Physical Properties Metric English Comments
Specific Gravity 1.06 g/cc
1.06 g/cc
ASTM D792
Density 1.09 g/cc
0.0394 lb/in³
ISO 1183
Moisture Absorption 0.200 %
0.200 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.55 %
0.55 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 7.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 7.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D1238
Melt Index of Compound 7.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 7.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 MVR [cm^3/10 min]; ISO 1133
8.0 g/10 min

@Load 5.00 kg,
Temperature 260 °C
 8.0 g/10 min

@Load 11.0 lb,
Temperature 500 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 95
95
ISO 2039-2
Tensile Strength at Break 30.0 MPa
4350 psi
Type I, 50 mm/min; ASTM D638
30.0 MPa
4350 psi
50 mm/min; ISO 527
Tensile Strength, Yield 38.0 MPa
5510 psi
Type I, 50 mm/min; ASTM D638
38.0 MPa
5510 psi
50 mm/min; ISO 527
Elongation at Break 4.0 %
4.0 %
Type I, 50 mm/min; ASTM D638
4.0 %
4.0 %
50 mm/min; ISO 527
Elongation at Yield 2.5 %
2.5 %
Type I, 50 mm/min; ASTM D638
2.5 %
2.5 %
50 mm/min; ISO 527
Tensile Modulus 1.79 GPa
260 ksi
5 mm/min; ASTM D638
1.90 GPa
276 ksi
1 mm/min; ISO 527
Flexural Yield Strength 50.0 MPa
7250 psi
2 mm/min; ISO 178
55.0 MPa
7980 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 1.79 GPa
260 ksi
1.3 mm/min, 50 mm span; ASTM D790
1.90 GPa
276 ksi
2 mm/min; ISO 178
Izod Impact, Notched 1.34 J/cm
2.51 ft-lb/in
ASTM D256
0.560 J/cm

@Temperature -30.0 °C
 1.05 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Notched (ISO) 12.0 kJ/m²
5.71 ft-lb/in²
80*10*4; ISO 180/1A
5.00 kJ/m²

@Temperature -30.0 °C
 2.38 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 1.20 J/cm²
5.71 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.400 J/cm²

@Temperature -30.0 °C
 1.90 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 17.0 J

@Temperature 23.0 °C
 12.5 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 86.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
 48.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
90.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 50.0 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 91.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
 51.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
100 µm/m-°C

@Temperature 23.0 - 60.0 °C
 55.6 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 88.0 °C
190 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 75.0 °C
167 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
77.0 °C

@Thickness 3.20 mm
 171 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Vicat Softening Point 86.0 °C
187 °F
Rate B/50; ISO 306
91.0 °C
196 °F
Rate B/120; ISO 306
99.0 °C
210 °F
Rate B/50; ASTM D1525
Descriptive Properties Value Comments
Ball Pressure Test, 75°C +/- 2°C PASSES
IEC 60695-10-2