Mitsubishi XantarÂ® C CF 107 Polycarbonate/ABS Blend

Category	Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer	Mitsubishi
Trade Name	Xantar®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Mitsubishi XantarÂ® C CF 107 Polycarbonate/ABS Blend.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

XantarÂ® materials are engineered for performance, consistency and reliability. This makes XantarÂ® resins ideal for interior automotive components, electrical equipment and consumer appliances where quality is a key requirement. The XantarÂ® range includes: clear and tinted grades for transparent applicationsreinforced materialsFlame retardant and halogen free typeslubricated materials for added wear resistanceMitsubishi Engineering Plastics acquired the XantarÂ® product line from DSM in 2010.

Physical Properties	Metric	English	Comments
Density	1.17 g/cc	0.0423 lb/inÂ³	ISO 1183
Water Absorption	0.60 %	0.60 %	Sim. to ISO 62
Moisture Absorption at Equilibrium	0.20 %	0.20 %	Humidity Absorption; Sim. to ISO 62
Melt Flow	58.5 g/10 min @Load 5.00 kg, Temperature 260 Â°C	58.5 g/10 min @Load 11.0 lb, Temperature 500 Â°F	Calculated from Volume Flow Rate of 50 cm<sup>3</sup>/10min.; ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	60.0 MPa	8700 psi	ISO 527-1/-2
Elongation at Break	>= 50 %	>= 50 %	ISO 527-1/-2
Elongation at Yield	4.0 %	4.0 %	ISO 527-1/-2
Tensile Modulus	2.85 GPa	413 ksi	ISO 527-1/-2
Flexural Strength	110 MPa	16000 psi	ISO 178
Flexural Modulus	2.80 GPa	406 ksi	ISO 178
Izod Impact, Notched (ISO)	35.0 kJ/mÂ² @Temperature 23.0 Â°C	16.7 ft-lb/inÂ² @Temperature 73.4 Â°F	ISO 180/4A
Charpy Impact Unnotched	NB @Temperature -30.0 Â°C	NB @Temperature -22.0 Â°F	ISO 179/1eU
	NB @Temperature 23.0 Â°C	NB @Temperature 73.4 Â°F	ISO 179/1eU

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	90.0 Â°C	194 Â°F	Ball Pressure Temperature; IEC 60695-10-2
Deflection Temperature at 1.8 MPa (264 psi)	90.0 Â°C	194 Â°F	ISO 75-1/-2
Vicat Softening Point	104 Â°C	219 Â°F	50Â°C/h 50N; ISO 306
Flammability, UL94	V-0 @Thickness 3.00 mm	V-0 @Thickness 0.118 in	IEC 60695-11-10
	V-0 @Thickness 1.60 mm	V-0 @Thickness 0.0630 in	IEC 60695-11-10
	5VB @Thickness 2.00 mm	5VB @Thickness 0.0787 in	IEC 60695-11-20
Oxygen Index	32 %	32 %	ISO 4589-1/-2
Glow Wire Test	750 Â°C @Thickness 1.50 mm	1380 Â°F @Thickness 0.0591 in	Glow Wire Ignition Temperature; IEC 60695-2-13
	750 Â°C @Thickness 3.00 mm	1380 Â°F @Thickness 0.118 in	Glow Wire Ignition Temperature; IEC 60695-2-13
	960 Â°C @Thickness 3.00 mm	1760 Â°F @Thickness 0.118 in	Glow Wire Flammability Index; IEC 60695-2-12
	960 Â°C @Thickness 1.50 mm	1760 Â°F @Thickness 0.0591 in	Glow Wire Flammability Index; IEC 60695-2-12

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+15 ohm-cm	>= 1.00e+15 ohm-cm	IEC 60093
Surface Resistance	>= 1.00e+15 ohm	>= 1.00e+15 ohm	IEC 60093
Dielectric Constant	3.0 @Frequency 1e+6 Hz	3.0 @Frequency 1e+6 Hz	IEC 60250
Comparative Tracking Index	400 - 599 V	400 - 599 V	PLC 1; UL 746A
	575 V	575 V	IEC 60112

Descriptive Properties	Value	Comments
Flame Retardant	Yes
Flame Retarding Agent	Yes
Injection molding	Yes
Release Agent	Yes
Without Fillers	Yes