PolyOne Lubri-Tech™ AT-000/02T Acetal - 2% PTFE (discontinued **)
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, PTFE Filled |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ AT-000/02T Acetal - 2% PTFE
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by PolyOne.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ASTM D792 |
| Water Absorption | 0.10 % | 0.10 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.015 - 0.020 cm/cm @Thickness 3.17 mm |
0.015 - 0.020 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 48.0 MPa | 6960 psi | ASTM D638 |
| Elongation at Break | 2.0 - 8.0 % | 2.0 - 8.0 % | ASTM D638 |
| Tensile Modulus | 2.60 GPa | 377 ksi | ASTM D638 |
| Flexural Yield Strength | 79.0 MPa | 11500 psi | ASTM D790 |
| Flexural Modulus | 2.60 GPa | 377 ksi | ASTM D790 |
| Izod Impact, Notched | 0.370 - 0.590 J/cm @Thickness 6.35 mm |
0.693 - 1.11 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 163 °C | 325 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 102 °C | 216 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 188 - 210 °C | 370 - 410 °F | Stock |
| Mold Temperature | 71.0 - 82.0 °C | 160 - 180 °F | |
| Drying Temperature | 71.0 °C | 160 °F |