PolyOne Dynalloy™ OBC8000-T40 Thermoplastic Elastomer (TPE)

Category Polymer , Thermoplastic , Elastomer, TPE
Manufacturer PolyOne Corporation
Trade Name Dynalloy™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Dynalloy™ OBC8000-T40 Thermoplastic Elastomer (TPE).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Dynalloy™ OBC8000-T40 is an easy processing, general processing TPE utilizing the unique rubber properties of Dow INFUSE™ Olefin Block Copolymers. Designed for a wide variety of applications, including applications requiring FDA compliances - Adhesion to Polypropylene - Enhanced Flow - Excellent Colorability - Warm, Non-tacky, RubberyColor concentrates with polypropylene (PP), ethylene vinyl acetate (EVA), or low density polyethylene (LDPE) carriers are most suitable for coloring Dynalloy™ OBC8000-T40. Improved color dispersion can be achieved by using higher melt flow concentrates (with a melt flow from 25 - 40 g/10 min). Typical loadings for color concentrates are 1% to 5% by weight. Liquid color can be used, but mineral oil based carriers may have a significant effect on the final hardness value. Concentrates based on PVC should not be used. A high color match consistency can be obtained by using precolored compounds available from GLS. The final determination of color concentrate suitability should be determined by customer trials. Purge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polystyrene (PS) or polypropylene (PP). Regrind levels up to 20% can be used with Dynalloy™ OBC8000-T40 with minimal property loss, provided that the regrind is free of contamination. To minimize losses during molding, the melt tempetature should remain as low as possible. The final determination of regrind effectiveness should be determined by the customer. Dynalloy™ OBC8000-T40 has good melt stability. Maximum residence times may vary, depending on the size of the barrel. Generally, the barrel should be emptied if it is idle for periods of 8 - 10 minutes or longer. Drying is not Required Injection Speed: 1 to 3 in/sec 1st Stage - Boost Pressure: 200 to 900 psi 2nd Stage - Hold Pressure: 20% of Boost Hold Time (Thick Part): 4 to 10 sec Hold Time (Thin Part): 1 to 4 secInformation provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 0.878 g/cc
0.878 g/cc
ASTM D792
Viscosity 8300 cP

@Shear Rate 11200 1/s,
Temperature 200 °C
8300 cP

@Shear Rate 11200 1/s,
Temperature 392 °F
ASTM D3835
37000 cP

@Shear Rate 1340 1/s,
Temperature 200 °C
37000 cP

@Shear Rate 1340 1/s,
Temperature 392 °F
ASTM D3835
Mechanical Properties Metric English Comments
Hardness, Shore A 43
43
10 sec; ASTM D2240
Tensile Strength at Break 3.10 MPa

@Temperature 23.0 °C
450 psi

@Temperature 73.4 °F
Die C2 hr; ASTM D412
Tensile Stress 1.05 MPa

@Strain 100 %,
Temperature 23.0 °C
152 psi

@Strain 100 %,
Temperature 73.4 °F
Die C2 hr; ASTM D412
1.57 MPa

@Strain 300 %,
Temperature 23.0 °C
228 psi

@Strain 300 %,
Temperature 73.4 °F
Die C2 hr; ASTM D412
Elongation at Break 790 %

@Temperature 23.0 °C
790 %

@Temperature 73.4 °F
Die C2 hr; ASTM D412
Compression Set 24 %

@Temperature 23.0 °C,
Time 79200 sec
24 %

@Temperature 73.4 °F,
Time 22.0 hour
ASTM D395B
Processing Properties Metric English Comments
Rear Barrel Temperature 166 - 188 °C
331 - 370 °F
Middle Barrel Temperature 177 - 199 °C
351 - 390 °F
Front Barrel Temperature 199 - 221 °C
390 - 430 °F
Nozzle Temperature 199 - 221 °C
390 - 430 °F
Melt Temperature 193 - 227 °C
379 - 441 °F
Mold Temperature 26.7 - 37.8 °C
80.1 - 100 °F
Back Pressure 0.000 - 0.552 MPa
0.000 - 80.1 psi
Screw Speed 50 - 100 rpm
50 - 100 rpm
Descriptive Properties Value Comments
Agency Ratings FDA Unspecified Rating
Appearance Translucent
Features Good Colorability
Good Flow
Forms Pellets
Generic Material TPE
Generic Name Thermoplastic Elastomer (TPE)
Manufacturer / Supplier GLS Thermoplastic Elastomers
Processing Method Extrusion
Injection Molding
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
RoHS Compliance RoHS Compliant
Suggested Max Regrind 20%