Polimeri Europa Greenflex® FF 45 Ethylene Vinyl Acetate Copolymer - Blown Film Extrusion

Category	Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer	Polimeri Europa (Former EniChem)
Trade Name	Greenflex®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Polimeri Europa Greenflex® FF 45 Ethylene Vinyl Acetate Copolymer - Blown Film Extrusion.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Greenflex FF 45 is an ethylene vinyl acetate copolymer (EVA) for blown film extrusion. Films produced with Greenflex FF 45 show high toughness.Main Applications: Greenflex FF 45 is recommended for the production of greenhouse film, stretch hood packaging and sanitary applications.Information provided by Polimeri Europa.

Physical Properties	Metric	English	Comments
Specific Gravity	0.935 g/cc	0.935 g/cc	ISO 1183
Vinyl Acetate Content	14 %	14 %	Internal Method
Thickness	30.0 - 150 microns	1.18 - 5.91 mil	Recommended
Melt Flow	0.70 g/10 min @Load 2.16 kg, Temperature 190 °C	0.70 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	92	92	ISO 868/A
Hardness, Shore D	39	39	ISO 868/A
Film Tensile Strength at Yield, MD	6.00 MPa	870 psi	ISO 527-3
Film Tensile Strength at Yield, TD	5.00 MPa	725 psi	ISO 527-3
Film Elongation at Break, MD	450 %	450 %	ISO 527-3
Film Elongation at Break, TD	700 %	700 %	ISO 527-3
Coefficient of Friction, Dynamic	>= 0.50	>= 0.50	ISO 8295
Elmendorf Tear Strength, MD	2.4456 g/micron	62.118 g/mil	ISO 6383-2
Elmendorf Tear Strength, TD	4.076 g/micron	103.5 g/mil	ISO 6383-2
Dart Drop Test	700 g	1.54 lb	F50; ISO 7765-1
Film Tensile Strength at Break, MD	31.0 MPa	4500 psi	ISO 527-3
Film Tensile Strength at Break, TD	29.0 MPa	4210 psi	ISO 527-3
1% Secant Modulus, MD	65.0 MPa	9430 psi	ISO 527-3
1% Secant Modulus, TD	70.0 MPa	10200 psi	ISO 527-3

Thermal Properties	Metric	English	Comments
Melting Point	93.0 °C	199 °F	Internal Method
Vicat Softening Point	73.0 °C @Load 1.00 kg	163 °F @Load 2.20 lb	ISO 306/A
Brittleness Temperature	<= -80.0 °C	<= -112 °F	ASTM D746

Optical Properties	Metric	English	Comments
Haze	1.5 %	1.5 %	ISO 14782
Gloss	83 %	83 %	45°; ASTM D2457