Polimeri Europa Clearflex® CM 406 Hexene Copolymer Linear Low Density Polyethylene

Category Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Hexene, Film Grade
Manufacturer Polimeri Europa (Former EniChem)
Trade Name Clearflex®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa Clearflex® CM 406 Hexene Copolymer Linear Low Density Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Clearflex CM 406 is a hexene copolymer linear low density polyethylene (C6-LLDPE), with antioxidants, suitable for cast film extrusion.Films manufactured with Clearflex CM 406 are characterized by high clarity, optimum elongation at break and optimum impact and tear resistance.Main Applications: Clearflex CM 406 is recommended for the production of low cling cast film with optimum optical properties and good mechanical resistance.Information provided by Polimeri Europa.
Physical Properties Metric English Comments
Specific Gravity 0.926 g/cc
0.926 g/cc
ISO 1183
Thickness 8.00 - 50.0 microns
0.315 - 1.97 mil
Recommended
Melt Flow 3.6 g/10 min

@Load 2.16 kg,
Temperature 190 °C
3.6 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 11.0 MPa
1600 psi
ISO 527-3
Film Tensile Strength at Yield, TD 11.0 MPa
1600 psi
ISO 527-3
Film Elongation at Break, MD 730 %
730 %
ISO 527-3
Film Elongation at Break, TD 850 %
850 %
ISO 527-3
Coefficient of Friction, Dynamic >= 0.50
>= 0.50
ISO 8295
Elmendorf Tear Strength, MD 8.152 g/micron
207.1 g/mil
ISO 6383-2
Elmendorf Tear Strength, TD 18.342 g/micron
465.89 g/mil
ISO 6383-2
Dart Drop Test 90.0 g
0.198 lb
F50; ISO 7765-1
Film Tensile Strength at Break, MD 36.0 MPa
5220 psi
ISO 527-3
Film Tensile Strength at Break, TD 30.0 MPa
4350 psi
ISO 527-3
1% Secant Modulus, MD 240 MPa
34800 psi
ISO 527-3
1% Secant Modulus, TD 250 MPa
36300 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 127 °C
261 °F
Internal method
Vicat Softening Point 103 °C

@Load 1.00 kg
217 °F

@Load 2.20 lb
ISO 306/A
Brittleness Temperature <= -70.0 °C
<= -94.0 °F
ASTM D746
Optical Properties Metric English Comments
Haze 4.0 %
4.0 %
ISO 14782
Gloss 85 %
85 %
45°; ASTM D2457
Transmission, Visible 90 %
90 %
clear; thickness not quantified