PolyOne Nymax™ GMF 604 40 UV Black 115 1 X 1 Polyamide 6 (Nylon 6)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | PolyOne Corporation |
| Trade Name | Nymax™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Nymax™ GMF 604 40 UV Black 115 1 X 1 Polyamide 6 (Nylon 6).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
The Nymax® GMF 600 Series of compounds are based upon nylon 6 resins and select combinations of glass fiber and mineral reinforcements offering a unique balance of physical property and part performance. These materials have been specifically formulated to offer ease of processing in most standard thermoplastic processing equipment.Molded Test Bars: Dry as MoldedInformation provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.48 g/cc | 1.48 g/cc | ASTM D792 |
| Density | 1.48 g/cc | 0.0535 lb/in³ | ISO 1183 |
| Water Absorption | 1.0 % | 1.0 % | 24h/23C; ISO 62 |
| 0.80 % @Thickness 3.18 mm |
0.80 % @Thickness 0.125 in |
@ 24 hrs; ASTM D570 | |
| Linear Mold Shrinkage | 0.0030 - 0.0040 cm/cm | 0.0030 - 0.0040 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 103 MPa | 14900 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Strength, Yield | 100 MPa | 14500 psi | ISO 527-2 |
| 117 MPa | 17000 psi | Type I, 5.1 mm/min; ASTM D638 | |
| Elongation at Break | 2.0 - 3.0 % | 2.0 - 3.0 % | Type I, 5.1 mm/min; ASTM D638 |
| 3.0 % | 3.0 % | ISO 527-2 | |
| Tensile Modulus | 7.58 GPa | 1100 ksi | ASTM D638 |
| 7.80 GPa | 1130 ksi | ISO 527-2 | |
| Flexural Strength | 172 MPa | 24900 psi | ASTM D790 |
| 180 MPa | 26100 psi | ISO 178 | |
| Flexural Modulus | 7.24 GPa | 1050 ksi | ASTM D790 |
| 7.50 GPa | 1090 ksi | ISO 178 | |
| Izod Impact, Notched | 0.640 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
1.20 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | Annealed; ISO 75-2/A |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Mold Temperature | 48.9 - 93.3 °C | 120 - 200 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 4.00 hour | 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additive | Heat Stabilizer | |
| UV Stabilizer | ||
| Appearance | Black | |
| Features | General Purpose | |
| Heat Stabilized | ||
| Filler / Reinforcement | GlassMineral, 40% Filler by Weight | |
| Forms | Pellets | |
| Generic Material | Nylon 6 | |
| Generic Name | Polyamide 6 (Nylon 6) | |
| Processing Method | Injection Molding | |
| Regional Availability | North America | |
| South America | ||
| Uses | Automotive Applications | |
| Construction Applications | ||
| Consumer Applications | ||
| General Purpose | ||
| Industrial Applications |