Plastics Group Polifil® GFRMPPCC-30 30% Glass Reinforced Polypropylene, High Impact

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler
Manufacturer	The Plastics Group of America
Trade Name	Polifil®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Plastics Group Polifil® GFRMPPCC-30 30% Glass Reinforced Polypropylene, High Impact.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Polifil® GFRMPPCC series compounds are high impact polypropylenes reinforced with chemically coupled glass fibers. This combination provides higher impact strength while retaining high stiffness.Applications: AppliancesElectrical componentsAutomotiveUtility products Standard processing techniques are applicable. Information provided by The Plastics Group.

Physical Properties	Metric	English	Comments
Density	1.13 g/cc	0.0408 lb/in³	ASTM D792
Filler Content	30 %	30 %	ASTM D2584
Linear Mold Shrinkage	0.0035 cm/cm @Thickness 1.59 mm	0.0035 in/in @Thickness 0.0625 in	ASTM D955
Melt Flow	5.0 - 10 g/10 min	5.0 - 10 g/10 min	230/2.16; May be specified; ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	68.9 MPa	10000 psi	ASTM D638
Elongation at Break	4.0 %	4.0 %	ASTM D638
Flexural Strength	83.4 MPa	12100 psi	ASTM D638
Flexural Modulus	3.86 GPa	560 ksi	Tangent; ASTM D790
Izod Impact, Notched	1.60 J/cm	3.00 ft-lb/in	At 73°F; ASTM D256
Gardner Impact	0.904 J	0.667 ft-lb	ASTM D3029

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	149 °C	300 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	132 °C	270 °F	ASTM D648

Users viewing this material also viewed the following: