Parker Chomerics Tecknit TeckBond™-NC Nickel Coated Graphite-Filled Adhesive

Category Polymer , Adhesive
Manufacturer Parker Chomerics Tecknit
Trade Name TeckBond™-NC
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Parker Chomerics Tecknit TeckBond™-NC Nickel Coated Graphite-Filled Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: TECKBOND-NC is a silicone rubber base filled with nickel coated graphite particles to produce a highly conductive one-component adhesive sealant. The system is an RTV moisture-cured compound which is ready to use without additional preparation or mixing. The compound cures at room temperature to form a flexible resilient conductive bond or sealant.Application Information: TECKBOND conductive adhesive-sealants are recommended wherever a flexible bond is required in a metal-to-silicone gasket application, such as TECKNIT NC-CONSIL®.Information provided by Chomerics
Mechanical Properties Metric English Comments
Shear Strength >= 0.689 MPa
>= 99.9 psi
Cured; ASTM D1002
Peel Strength >= 0.526 kN/m
>= 3.00 pli
Silicone Aluminum; Cured; ASTM D1876
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 200 °C
392 °F
Cured
Minimum Service Temperature, Air -55.0 °C
-67.0 °F
Cured
Shrinkage <= 1.0 %
<= 1.0 %
Cured
Electrical Properties Metric English Comments
Volume Resistivity <= 0.50 ohm-cm
<= 0.50 ohm-cm
Cured; QA-1038
Processing Properties Metric English Comments
Dry Time 1.50 hour
1.50 hour
Tack Free
Cure Time 4320 min

@Temperature 25.0 °C
72.0 hour

@Temperature 77.0 °F
50%; Recommended for 1/8" dia bead
10100 min

@Temperature 25.0 °C
168 hour

@Temperature 77.0 °F
50%; Full Cure
Shelf Life 9.00 Month
9.00 Month
Unopened Container
Descriptive Properties Value Comments
Color Dark Gray
Consistency Thick Paste
Filler Nickel coated graphite
Final Condition Flexible
Number of Components One
Resin Silicone