Old Hickory UltraCast Slurry PC-2000 Kentucky Ball Clay

Category Ceramic , Clay , Ball Clay
Manufacturer Old Hickory Clay Co.
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Old Hickory UltraCast Slurry PC-2000 Kentucky Ball Clay.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
These popular slurry grades are shipped at 60% solids content and deflocculated with sodium silicate to maintain stable rheology characteristics. All the above grades are suitable for a variety of ceramic casting formulations ranging from standards bench cast to pressure cast and capillary type production systems. High permeability with good strength and plasticity are key properties of these slurry grade clays.Information provided by Old Hickory Clay Company
Physical Properties Metric English Comments
Specific Gravity 1.585 - 1.60 g/cc
1.585 - 1.60 g/cc
Solids Content 60 - 61 %
60 - 61 %
Particle Size 0.50 µm
0.50 µm
29% of particles less than
1.0 µm
1.0 µm
41% of particles less than
2.12 µm
2.12 µm
Median particle diameter
<= 5.0 µm
<= 5.0 µm
71% of particles less than
pH 3.0 - 5.5

@Temperature 32.2 °C
3.0 - 5.5

@Temperature 90.0 °F
Soluble Sulfates 300 - 500 ppm
300 - 500 ppm
Specific Surface Area 16.5 m²/g
16.5 m²/g
Viscosity 100 - 300 cP

@Temperature 32.2 °C
100 - 300 cP

@Temperature 90.0 °F
Mechanical Properties Metric English Comments
Modulus of Rupture 0.00431 GPa
0.625 ksi
Dry Modulus of Rupture, 50% clay/50% flint
Component Elements Properties Metric English Comments
Al2O3 25.14 %
25.14 %
CaO 0.16 %
0.16 %
Carbon, C 1.1 %
1.1 %
Fe2O3 1.41 %
1.41 %
K2O 1.49 %
1.49 %
Loss on Ignition(%) 9.08 %
9.08 %
MgO 0.48 %
0.48 %
Na2O 0.11 %
0.11 %
SiO2 60.59 %
60.59 %
TiO2 1.62 %
1.62 %
Descriptive Properties Value Comments
CEC/MBI (meg/100 ml) 6.8
Deflocculant Type Sodium Silicate (N Brand)
Drop On Curve (cps) 30-120
at 90°F, Brookfield, 100 rpm, No. 3 Spindle