LyondellBasell Hostacomâ„¢ 6551 Polypropylene Homopolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded |
| Manufacturer | LyondellBasell |
| Trade Name | Hostacom™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Hostacomâ„¢ 6551 Polypropylene Homopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Hostacomâ„¢ 6551 conventional melt flow, 1,300 MPa flexural modulus, precolored polypropylene homopolymer has a good combination of strength, stiffness, impact and heat resistance. It was designed for a variety of industrial and consumer applications. Uses: Electrical parts, appliances, industrial applications, consumer applicationsInformation provided by Basell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.942 g/cc | 0.0340 lb/in³ | ASTM D792 |
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
Condition L; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 98 | 98 | ASTM D 785 |
| Tensile Strength at Break | 14.0 MPa | 2030 psi | ASTM D 638 |
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D 638 |
| Elongation at Break | 350 % | 350 % | ASTM D 638 |
| Elongation at Yield | 7.0 % | 7.0 % | ASTM D 638 |
| Flexural Modulus | 1.30 GPa | 189 ksi | procedure A; ASTM D790 |
| Izod Impact, Notched | 0.529 J/cm | 0.990 ft-lb/in | 73°F; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 81.1 °C | 178 °F | Unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Polimeri Europa Dutral® CO 043 Ethylene - Propylene
- Rogers Corporation Theta® MCL-HE-679G Laminate, GHA-679G Prepreg Halogen-Free, Low Dielectric Constant, High heat Resistant Multi-Layer Circuit Material
- Quadrant EPP Proteus® HDPE - High Density Polyethylene (ASTM Product Data Sheet)
- Kazanorgsintez Aluminum Hydroxychloride
- Lehmann & Voss LUVOCOM® 6-7833 Polyamide 12, with PTFE, lubricant modified
- Ineos L10G-00 Polypropylene Impact Copolymer
- Michelman® DigiGuard® Gloss 100 Water based overprint varnish
- Thermoseal KLINGERSIL® C-4500 Carbon Fiber Reinforced Gasketing
- BASF Neopolen® P 9230 D 0.07 g/cc Core density; Expanded Polypropylene (Europe)
Copyright © lookpolymers.com All Rights Reserved