Thermoseal KLINGERSIL® C-4500 Carbon Fiber Reinforced Gasketing
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | Thermoseal Inc. |
| Trade Name | KLINGERSIL® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Thermoseal KLINGERSIL® C-4500 Carbon Fiber Reinforced Gasketing.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Carbon FiberNitrile BinderHigh TemperatureHigh Internal PressureSuitable for a Wide Range of Chemical ApplicationsGood Steam SheetInformation provided by Thermoseal Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ASTM F1315 |
| Thickness | 1588 microns | 62.52 mil | Thickness tested |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 1.50 kV/mm | 38.1 kV/in | ASTM D149-95a |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black | (Top/Bottom) |
| Compressibility | 12 percent | ASTM F36J |
| Creep Relaxation | 20 percent | 1/32", ASTM F38B |
| Gas Permeability | <1.0 ml/min | DIN 3535/6 |
| Klinger Hot Compression Test | 10 percent | Initial, Thickness Decrease 73°F (23°C) |
| 15 percent | Additional, Thickness Decrease 572°F (300°C) | |
| Leachable Chloride Content | 200 ppm | FSA Method (Typical) |
| Recovery | >60 percent | ASTM F36J |
| Sealability | <0.30 ml/hr | 1/32", ASTM F37A |
| Thickness Increase | 0-3% | ASTM Oil IRM903, 5h/300°F (149°C) |
| 0-5% | ASTM F146 after immersion in ASTM Oil 1, 5h/300°F (149°C) | |
| 0-5% | ASTM Fuel A, 5h/73°F (23°C) | |
| 0-5% | ASTM Fuel B, 5h/73°F (23°C) | |
| Weight Increase | <10% | ASTM F146 after immersion in Fuel B 5h/73°F (23°C) |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 123X PC Copolymer (Europe-Africa-Middle East)
- Fujipoly Industries Sarcon® XR-e Gap Filler Pad
- Momentive Performance Materials Siloprenâ„¢ LSR 2742 Liquid Silicone Rubber - Self-Bonding
- Solvay Specialty Polymers Ryton® R-4-200BL Polyphenylene Sulfide (PPS), 40% Glass Fiber
- Sinotek Materials MD-2 Graphite Emulsion
- Borealis Borstar® CB9600 HDPE for Extrusion Coating
- Williams Advanced Alloys WS238 Solder
- REXtac Rextac® RT 5224 Amorphous Polyalphaolefin (APAO)
Copyright © lookpolymers.com All Rights Reserved