Lanxess Durethan® DP 1441/40 H2.0 EF 900116 Nylon 6, 40% Glass Fiber + Mineral
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® DP 1441/40 H2.0 EF 900116 Nylon 6, 40% Glass Fiber + Mineral.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, injection molding grade, 40% glass fibers/mineral, good heat-ageing resistance, good surface, good flowability (Easy Flow), low warpage
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | ISO 1183 |
| Melt Flow | 86 g/10 min @Load 5.00 kg, Temperature 270 °C |
86 g/10 min @Load 11.0 lb, Temperature 518 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.0 MPa | 9430 psi | Conditioned; ISO 527-1/-2 |
| 135 MPa | 19600 psi | ISO 527-1/-2 | |
| Elongation at Break | 2.8 % | 2.8 % | ISO 527-1/-2 |
| 8.7 % | 8.7 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 4.50 GPa | 653 ksi | Conditioned; ISO 527-1/-2 |
| 8.50 GPa | 1230 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 4.00 J/cm² @Temperature 23.0 °C |
19.0 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| 4.50 J/cm² @Temperature -30.0 °C |
21.4 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179/1eU | |
| 6.50 J/cm² @Temperature 23.0 °C |
30.9 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | 0.500 J/cm² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| 0.800 J/cm² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C | 16.7 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
IEC 60695-11-10 |
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additives | Release agent | |
| Features | Heat stabilized or stable to heat | |
| Form | Pellets | |
| ISO Shortname | ISO 1874-PA 6, MH,10-090,GFM40 | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Gharda Chemicals Gafone™ 3610GM20 Polyethersulfone (PES) (discontinued **)
- Lubrizol Advanced Materials Pearlstick® 46-73/19 Polyester based TPU (discontinued **)
- Karina 4000/35-IE MBPEBD Green Color Concentrate
- Samsung Cheil Industries Starex® CR-0760 ABS, Unreinforced
- CeramTec DN 70 Dispersion Ceramic, Al2O3-ZrO2
- A. Schulman POLYBATCH™ Silver 70100 Concentrate Based In LDPE
- Constellium Planoxal® 60 Aluminum plate
- ChevronTexaco Canopus® 32
- DuPont Performance Polymers Zytel® 103FHS BKB038 Nylon 66 (Unverified Data**)
- SK Chemicals SKYTHANE® 398A S series Polyurethane
Copyright © lookpolymers.com All Rights Reserved