LNP Lubricomp® OCL-4536 Polyphenylene Sulfide, Carbon Fiber Reinforced, PTFE + Silicone Lubricant  (discontinu

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with Carbon Fiber + PTFE Filler
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LNP Lubricomp® OCL-4536 Polyphenylene Sulfide, Carbon Fiber Reinforced, PTFE + Silicone Lubricant  (discontinu.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: LubricatedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
Physical Properties Metric English Comments
Specific Gravity 1.49 g/cc
1.49 g/cc
Method A; ASTM D792
Mechanical Properties Metric English Comments
Tensile Strength at Break 119 MPa
17300 psi
ASTM D638
Elongation at Break 1.6 %
1.6 %
ASTM D638
Flexural Strength 228 MPa
33100 psi
ASTM D790
Flexural Modulus 20.1 GPa
2920 ksi
ASTM D790
Izod Impact, Notched 0.374 J/cm

@Thickness 3.18 mm
0.701 ft-lb/in

@Thickness 0.125 in
ASTM D256
Izod Impact, Unnotched 3.20 J/cm

@Thickness 3.18 mm
5.99 ft-lb/in

@Thickness 0.125 in
ASTM D256
Coefficient of Friction, Dynamic 0.36
0.36
vs. Steel - @ 40 psi, 50 ft/min, tested in accordance with LNP WI-0687; ASTM D1894
Coefficient of Friction, Static 0.30
0.30
vs. Steel @ 40 psi, tested in accordance with LNP WI-0687; ASTM D1894
K (wear) Factor 30.2 x 10-8 mm³/N-M
15.0 x 10-10 in³-min/ft-lb-hr
40psi, 50ft/min; tested in accordance with LNP WI-0687
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 259 °C
498 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Melt Temperature 316 - 321 °C
601 - 610 °F
Mold Temperature 135 - 163 °C
275 - 325 °F
Drying Temperature 121 - 149 °C
250 - 300 °F
Dry Time 4 hour
4 hour
Back Pressure 0.172 - 0.345 MPa
24.9 - 50.0 psi