LATI Latistat 67-08 PA66, Impact Modified

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade
Manufacturer	LATI
Trade Name	Latistat
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latistat 67-08 PA66, Impact Modified.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Dissipative product based on Polyamide 66 (PA66), impact modified. Unfilled.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.16 g/cc	0.0419 lb/inÂ³
Linear Mold Shrinkage, Flow	0.013 - 0.0165 cm/cm	0.013 - 0.0165 in/in
Linear Mold Shrinkage, Transverse	0.013 - 0.016 cm/cm	0.013 - 0.016 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	50.0 MPa	7250 psi
Elongation at Break	15 %	15 %
Tensile Modulus	2.30 GPa	334 ksi
Charpy Impact Unnotched	NB	NB
Charpy Impact, Notched	0.750 J/cmÂ²	3.57 ft-lb/inÂ²

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	185 Â°C	365 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	65.0 Â°C	149 Â°F
Vicat Softening Point	190 Â°C @Load 5.00 kg	374 Â°F @Load 11.0 lb

Electrical Properties	Metric	English	Comments
Volume Resistivity	250000 ohm-cm	250000 ohm-cm
Surface Resistance	250000 ohm	250000 ohm

Processing Properties	Metric	English
Melt Temperature	260 - 290 Â°C	500 - 554 Â°F
Mold Temperature	60.0 - 80.0 Â°C	140 - 176 Â°F
Drying Temperature	90.0 - 100 Â°C @Time 10800 sec	194 - 212 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa