LATI Latilub 57-30GRTS G/20 PPA, 20% Glass Fiber Reinforced

Category	Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 20% Glass Fiber Reinforced
Manufacturer	LATI
Trade Name	Latilub
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latilub 57-30GRTS G/20 PPA, 20% Glass Fiber Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Self-lubricating product based on Semi-aromatic polyamide (PPA). Glass fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.54 g/cc	0.0556 lb/inÂ³
Linear Mold Shrinkage, Flow	0.0050 - 0.0080 cm/cm	0.0050 - 0.0080 in/in
Linear Mold Shrinkage, Transverse	0.012 - 0.016 cm/cm	0.012 - 0.016 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	115 MPa	16700 psi
Elongation at Break	1.5 %	1.5 %
Tensile Modulus	11.0 GPa	1600 ksi
Charpy Impact Unnotched	2.00 J/cmÂ²	9.52 ft-lb/inÂ²
Charpy Impact, Notched	0.650 J/cmÂ²	3.09 ft-lb/inÂ²
Coefficient of Friction, Dynamic	0.22	0.22
Coefficient of Friction, Static	0.24	0.24
K (wear) Factor	8.00 x 10^-8 mmÂ³/N-M	3.97 x 10^-10 inÂ³-min/ft-lb-hr

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	295 Â°C	563 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	275 Â°C	527 Â°F
Vicat Softening Point	245 Â°C @Load 5.00 kg	473 Â°F @Load 11.0 lb

Processing Properties	Metric	English
Melt Temperature	310 - 330 Â°C	590 - 626 Â°F
Mold Temperature	150 - 170 Â°C	302 - 338 Â°F
Drying Temperature	120 - 130 Â°C @Time 10800 sec	248 - 266 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa

Users viewing this material also viewed the following: