LATI Latilub 52/30-15T G/30 PP Homopolymer, 30% Glass Fiber Reinforced

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler
Manufacturer	LATI
Trade Name	Latilub
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latilub 52/30-15T G/30 PP Homopolymer, 30% Glass Fiber Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Self-lubricating product based on Polypropylene homopolymer (PPh). PTFE. Glass fibersAvailability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.25 g/cc	0.0452 lb/inÂ³
Linear Mold Shrinkage, Flow	0.0040 - 0.0065 cm/cm	0.0040 - 0.0065 in/in
Linear Mold Shrinkage, Transverse	0.010 - 0.013 cm/cm	0.010 - 0.013 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	80.0 MPa	11600 psi
Elongation at Break	2.8 %	2.8 %
Tensile Modulus	6.70 GPa	972 ksi
Charpy Impact Unnotched	4.00 J/cmÂ²	19.0 ft-lb/inÂ²
Charpy Impact, Notched	0.700 J/cmÂ²	3.33 ft-lb/inÂ²
Coefficient of Friction, Dynamic	0.10	0.10
Coefficient of Friction, Static	0.16	0.16
K (wear) Factor	12.0 x 10^-8 mmÂ³/N-M	5.96 x 10^-10 inÂ³-min/ft-lb-hr

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	160 Â°C	320 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	145 Â°C	293 Â°F
Vicat Softening Point	130 Â°C @Load 5.00 kg	266 Â°F @Load 11.0 lb

Processing Properties	Metric	English
Melt Temperature	220 - 250 Â°C	428 - 482 Â°F
Mold Temperature	40.0 - 60.0 Â°C	104 - 140 Â°F
Drying Temperature	80.0 - 90.0 Â°C @Time 10800 sec	176 - 194 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa