LATI Latamid 66 E21 PA 66, Impact Modified

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade
Manufacturer LATI
Trade Name Latamid
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latamid 66 E21 PA 66, Impact Modified.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 66 (PA66). Toughened. Good impact resistance.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.07 g/cc
0.0387 lb/in³
Linear Mold Shrinkage, Flow 0.013 - 0.0165 cm/cm
0.013 - 0.0165 in/in
Linear Mold Shrinkage, Transverse 0.013 - 0.016 cm/cm
0.013 - 0.016 in/in
Mechanical Properties Metric English Comments
Elongation at Break >= 100 %

@Temperature 23.0 °C
 >= 100 %

@Temperature 73.4 °F
>= 100 %

@Temperature 60.0 °C
 >= 100 %

@Temperature 140 °F
>= 100 %

@Temperature 90.0 °C
 >= 100 %

@Temperature 194 °F
>= 100 %

@Temperature 120 °C
 >= 100 %

@Temperature 248 °F
>= 100 %

@Temperature 150 °C
 >= 100 %

@Temperature 302 °F
Elongation at Yield 5.0 %
5.0 %
Tensile Modulus 0.180 GPa

@Temperature 150 °C
 26.1 ksi

@Temperature 302 °F
0.200 GPa

@Temperature 120 °C
 29.0 ksi

@Temperature 248 °F
0.330 GPa

@Temperature 90.0 °C
 47.9 ksi

@Temperature 194 °F
0.500 GPa

@Temperature 60.0 °C
 72.5 ksi

@Temperature 140 °F
1.50 GPa

@Temperature 23.0 °C
 218 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
NB

@Temperature -20.0 °C
 NB

@Temperature -4.00 °F
Charpy Impact, Notched 2.00 J/cm²

@Temperature -20.0 °C
 9.52 ft-lb/in²

@Temperature -4.00 °F
10.0 J/cm²

@Temperature 23.0 °C
 47.6 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 90.0 °C
194 °F
Deflection Temperature at 0.46 MPa (66 psi) 145 °C
293 °F
Deflection Temperature at 1.8 MPa (264 psi) 55.0 °C
131 °F
Vicat Softening Point 200 °C

@Load 5.00 kg
 392 °F

@Load 11.0 lb
Processing Properties Metric English Comments
Melt Temperature 260 - 290 °C
500 - 554 °F
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa