Ineos Styrenics Polystyrene 476M Q598 (NAFTA)

Category Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified
Manufacturer Ineos Styrenics
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ineos Styrenics Polystyrene 476M Q598 (NAFTA).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High-impact grade of polystyrene with good ESCR designed to provide uniform melt flow for excellent processability.Information provided by BASF.Ineos Styrenics purchased this product line from BASF in 2005.
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
Moisture Absorption at Equilibrium <= 0.10 %
<= 0.10 %
Water Absorption at Saturation <= 0.10 %
<= 0.10 %
Linear Mold Shrinkage 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
ASTM D955
Melt Flow 3.2 g/10 min

@Load 5.00 kg,
Temperature 200 °C
 3.2 g/10 min

@Load 11.0 lb,
Temperature 392 °F
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 23.0 MPa
3340 psi
Tensile Strength, Yield 21.0 MPa
3050 psi
Elongation at Break 60 %
60 %
Tensile Modulus 1.38 GPa
200 ksi
Flexural Modulus 1.66 GPa
241 ksi
Izod Impact, Notched 1.55 J/cm
2.90 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C
185 °F
Vicat Softening Point 99.0 °C
210 °F
Flammability, UL94 HB

@Thickness 1.00 mm
 HB

@Thickness 0.0394 in
Optical Properties Metric English Comments
Gloss 30 %
30 %
Processing Properties Metric English Comments
Processing Temperature 200 - 230 °C
392 - 446 °F
Extrusion
180 - 280 °C
356 - 536 °F
Molding