ExxonMobil Label-Lyte™ 30LL666 OPP Film
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Label-Lyte™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Label-Lyte™ 30LL666 OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: A transparent, high gloss, two side acrylic coated BOPP film for reel-fed wrap-around labeling applications.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features: Superb gloss and transparencyExceptional printabilityExcellent hot melt anchorageHigh consistency and stability of surface propertiesExcellent machine performanceHigh resistance to elongation on labeling machineGood mold resistanceNot humidity resistantFeatures:Acrylic CoatedApplications:Beverage, AlcoholicBeverage, Carbonated Beverage, Mineral Waters Dairy ProductsHealth and Beauty CareUses: Reel-Fed LabelsProcessing Method: Inner Web Adhesion Lamination, Outer Web Adhesion Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing, Surface Print Unsupported and Water-based Flexographic PrintingInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Thickness | 30.5 microns | 1.20 mil | ExxonMobil Method |
| Coating Weight | 27.7 g/m² | 17.3 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 200 % | 200 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Elongation at Break, TD | 65 % | 65 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Modulus of Elasticity | 2.20 GPa | 319 ksi | MD; ExxonMobil Method |
| 3.50 GPa | 508 ksi | TD; ExxonMobil Method | |
| Coefficient of Friction | 0.25 | 0.25 | Acrylic; ExxonMobil Method |
| Film Tensile Strength at Break, MD | 135 MPa | 19600 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 275 MPa | 39900 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 5.0 % @Temperature 135 °C, Time 432 sec |
5.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Shrinkage, TD | 5.0 % @Temperature 135 °C, Time 432 sec |
5.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.3 % | 1.3 % | ExxonMobil Method |
| Gloss | 85 % | 85 % | 45°; ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Yield | 25000 in2/lb |
Users viewing this material also viewed the following:
- NIZHNEKAMSKNEFTEKHIM PP 4340R (EP2Z29G) Propylene and Ethylene Copolymer
- LATI LASTIROL R G/30 30% Glass Fiber Reinforced Polystyrene (PS) (discontinued **)
- NOVA Chemicals Sclair® 10B Octene VLDPE Film Resin (discontinued **)
- Chevron Phillips HiD® 9410 HDPE Blow Molding Resin (discontinued **)
- Kostat ICP-STAT ICD-1000 PC Sheet
- Teknor Apex Elexar® EL 3954-70 Thermoplastic Elastomer
- Dow Corning SILASTIC® T-4 RTV SILICONE RUBBER BASE & T-4 O CURING AGENT
- ChevronTexaco Regal® 460
Copyright © lookpolymers.com All Rights Reserved