ExxonMobil LD 135.09 Cast Packaging Film Resin (discontinued **)

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil LD 135.09 Cast Packaging Film Resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LD 135.09 is a homopolymer film resin with good clarity. It is suitable for processing in cast film equipment. Applications include food packaging, light to medium duty bags, and textile packaging.Information provided by ExxonMobil Chemical

Physical Properties	Metric	English	Comments
Density	0.921 g/cc	0.0333 lb/in³	ExxonMobil Method
Thickness	38.1 microns	1.50 mil
Melt Flow	3.0 g/10 min	3.0 g/10 min	ExxonMobil Method

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	6.89 MPa	1000 psi	at 2% offset; ASTM D882
Film Tensile Strength at Yield, TD	6.21 MPa	900 psi	at 2% offset; ASTM D882
Film Elongation at Break, MD	290 %	290 %	ASTM D882
Film Elongation at Break, TD	660 %	660 %	ASTM D882
Elmendorf Tear Strength, MD	7.09 g/micron	180 g/mil	ASTM D1922
Elmendorf Tear Strength, TD	3.94 g/micron	100 g/mil	ASTM D1922
Dart Drop	2.36 g/micron	60.0 g/mil	ASTM D1709
Film Tensile Strength at Break, MD	31.0 MPa	4500 psi	ASTM D882
Film Tensile Strength at Break, TD	17.9 MPa	2600 psi	ASTM D882
1% Secant Modulus, MD	145 MPa	21000 psi	ASTM D882
1% Secant Modulus, TD	152 MPa	22000 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	110 °C	230 °F	Peak Melting Temperature; ExxonMobil Method

Optical Properties	Metric	English	Comments
Haze	3.1 %	3.1 %	ASTM D1003
Gloss	75 %	75 %	45°; ASTM D2457

Descriptive Properties	Value	Comments
Features	Thermal Stabilizer