ExxonMobil HD 8760.29 Rotational Molding Resin

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Rotational Molding Grade
Manufacturer Exxon Chemical
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil HD 8760.29 Rotational Molding Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: HD 8760 is a high density hexene copolymer designed to offer outstanding stiffness and processability. This resin is ideally suited for applications that require the optimum balance of stiffness, processability and surface appearance.Availability: Latin America, North America and South America Additive: Long Term UV-15 Stabilizer: YesApplications: Consumer ArticlesRV tanksInformation provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.948 g/cc
0.0342 lb/in³
ASTM D4883
ESCR 100% Igepal® 10 hour
10 hour
ASTM D1693 Condition A
ESCR 10% Igepal® 8.0 hour
8.0 hour
ASTM D1693 Condition A
Melt Flow 5.00 g/10 min

@Load 2.16 kg,
Temperature 190 °C
5.00 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 23.4 MPa
3400 psi
2.0 in/min; ASTM D638
Elongation at Yield 20 %
20 %
2.0 in/min; ASTM D638
Flexural Modulus 1.03 GPa
150 ksi
1% Secant; ASTM D790
Impact Test 78.6 J

@Thickness 3.17 mm,
Temperature -40.0 °C
58.0 ft-lb

@Thickness 0.125 in,
Temperature -40.0 °F
ARM
176 J

@Thickness 6.35 mm,
Temperature -40.0 °C
130 ft-lb

@Thickness 0.250 in,
Temperature -40.0 °F
ARM
Thermal Properties Metric English Comments
Melting Point 131 °C
268 °F
ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 74.0 °C
165 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 43.0 °C
109 °F
ASTM D648
Descriptive Properties Value Comments
Features Long Term UV 8 Stabilization
Form Pellet