ExxonMobil Escorene® LD 720.62 Specialty Film Resin

Category Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer Exxon Chemical
Trade Name Escorene®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Escorene® LD 720.62 Specialty Film Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Escorene Ultra LD 720 resins are high vinyl acetate copolymer specialty film resins designed for applications requiring outstanding heat sealability, along with excellent strength properties and toughness.These resins are also used in specialized molding applications.Availability: Latin America, North America and South America Additive: Antiblock: NoSlip: No Thermal Stabilizer: Yes Applications:Heat Seal LayerInjection MoldingShoe SolesInformation provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.941 g/cc
0.0340 lb/in³
ExxonMobil Method
Vinyl Acetate Content 18.5 %
18.5 %
ExxonMobil Method
Melt Flow 1.60 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.60 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ExxonMobil Method
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 180 %
180 %
ASTM D882
Film Elongation at Break, TD 650 %
650 %
ASTM D882
Elmendorf Tear Strength MD 40 g
40 g
ASTM D1922
Elmendorf Tear Strength TD 80 g
80 g
ASTM D1922
Dart Drop Test 370 g
0.816 lb
ASTM D1709A
Film Tensile Strength at Break, MD 26.9 MPa
3900 psi
ASTM D882
Film Tensile Strength at Break, TD 27.6 MPa
4000 psi
ASTM D882
1% Secant Modulus, MD 65.5 MPa
9500 psi
ASTM D882
1% Secant Modulus, TD 68.9 MPa
10000 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 86.1 °C
187 °F
Peak Melting Temperature; ExxonMobil Method
Vicat Softening Point 62.2 °C
144 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 28 %
28 %
ASTM D1003
Gloss 49 %
49 %
45°; ASTM D2457