DuPont Performance Polymers Hypalon® 40 Chlorosulfonated Polyethylene Rubber, Carbon Black Filled Compound  (d

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Rubber or Thermoset Elastomer (TSE) , Chlorosulfonated Polyethylene Rubber
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Hypalon® 40 Chlorosulfonated Polyethylene Rubber, Carbon Black Filled Compound  (d.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Carbon black compound with 100 parts Hypalon; 27.8 parts sublimed litharge dispersion; 55 parts carbon black; 55 parts aromatic process oil; 0.5 parts MTBS; and 2 parts Tetrone® A rubber accelerator (from DuPont Dow Elastomers). Physical property data below (except mooney viscosity) are for vulcanizate cured 30 min. at 153°C. MatWeb has other entries for different compounds of this Hypalon grade.General Hypalon® Information: Vulcanizates of this chlorosulfonated polyethylene synthetic rubber are highly resistant to ozone, oxygen, weather, heat, oil, and chemicals. Hypalon resists discoloration on exposure to light and is widely used in light-colored vulcanizates. It can be compounded to give excellent mechanical properties. Several grades are available, all of which may be processed and used in the usual manner for solid elastomeric vulcanizates. Various grades of Hypalon have been used in single-ply roofing systems; auto power steering and oil cooler hoses; chemical-resistant liners; cable sheathing; and other coatings.Information provided by DuPont Dow Elastomers.This former DuPont Dow Elastomers product line is now produced by DuPont Performance Elastomers.
Physical Properties Metric English Comments
Mooney Viscosity 42

@Temperature 100 °C
42

@Temperature 212 °F
ML 1+4.  Stock property.; ASTM D1646-81
Mechanical Properties Metric English Comments
Hardness, Shore A 67
67
ASTM D2240-81
Tensile Strength, Ultimate 20.0 MPa
2900 psi
ASTM D412-80
Elongation at Break 310 %
310 %
ASTM D412-80
100% Modulus 0.00520 GPa
0.754 ksi
ASTM D412-80
Resilience 55
55
% Yerzley; ASTM D945-77
Graves Tear Strength 180 kN/m
1030 pli
Die C; ASTM D642-54
Abrasion 380
380
NBS Abrasion Index; ASTM D1630-74.
Compression Set 12 %

@Temperature 70.0 °C
12 %

@Temperature 158 °F
22 hr at 70°C original. Method B. ASTM D395-69.
Thermal Properties Metric English Comments
Minimum Service Temperature, Air -57.0 °C
-70.6 °F
Brittleness Temperature
Brittleness Temperature -57.0 °C
-70.6 °F
Wide variability between samples is observed.; ASTM D746
Clash Berg Stiffness Temperature -20.0 °C
-4.00 °F
T-10000 Torsional stiffness ASTM D1043-72(1981)