Equate EFDA-7047 LLDPE Film Extrusion Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer Equate
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Equate EFDA-7047 LLDPE Film Extrusion Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
EFDA-7047 is a linear low-density polyethylene resin for tubular blown film extrusion. Films made from this resin have good toughness, high tensile strength and puncture resistance. EFDA-7047 does not contain any slip or antiblocking agent.Applications: Industrial linersBlown film stretch wrapHeavy-duty filmsGeneral-purpose blown films for a variety of applications.Information provided by Equate
Physical Properties Metric English Comments
Bulk Density 0.538 g/cc
0.0194 lb/in³
ASTM D1895
Density 0.918 g/cc
0.0332 lb/in³
ASTM D792
Thickness 25.0 microns
0.984 mil
As Tested
Melt Flow 1.0 g/10 min

@Load 2.16 kg
1.0 g/10 min

@Load 4.76 lb
ASTM D1238
Mechanical Properties Metric English Comments
Elmendorf Tear Strength, MD 35.0 g/micron

@Thickness 0.0250 mm
889 g/mil

@Thickness 0.000984 in
ASTM D1922
Elmendorf Tear Strength, TD 26.0 g/micron

@Thickness 0.0250 mm
660 g/mil

@Thickness 0.000984 in
ASTM D1922
Dart Drop 4.20 g/micron

@Thickness 0.0250 mm
107 g/mil

@Thickness 0.000984 in
ASTM D1709 A
Dart Drop Test 105 g
0.232 lb
F50; ASTM D1709 A
Film Tensile Strength at Break, MD 34.0 MPa

@Thickness 0.0250 mm
4930 psi

@Thickness 0.000984 in
ASTM D882
Film Tensile Strength at Break, TD 26.0 MPa

@Thickness 0.0250 mm
3770 psi

@Thickness 0.000984 in
ASTM D882
1% Secant Modulus, MD 193 MPa

@Thickness 0.0250 mm
28000 psi

@Thickness 0.000984 in
ASTM D882
1% Secant Modulus, TD 221 MPa

@Thickness 0.0250 mm
32100 psi

@Thickness 0.000984 in
ASTM D882
Thermal Properties Metric English Comments
Melting Point 124 °C
255 °F
Equate Test Method
Optical Properties Metric English Comments
Haze 11 %
11 %
ASTM D1003
Gloss 65 %
65 %
45°; ASTM D2457
Processing Properties Metric English Comments
Blow-up Ratio (BUR) 2.0
2.0
2:1 As Tested
Descriptive Properties Value Comments
Puncture Energy 70 J/mm
Equate Test Method