Polymer Property : Film Tensile Strength at Break, TD = 26.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, TD	26.0 MPa	3770 psi	ISO 527-3
Polimeri Europa Clearflex® CL D0 Very Low Density Polyethylene Clearflex CL D0 is a linear low density polyethylene, with antioxidants, characterized by a very low density (VLDPE).This resin is produced with a proprietary technology. Stretch films manufactured..
Film Tensile Strength at Break, TD	26.0 MPa	3770 psi	ISO 527-3
Polimeri Europa Riblene® FC 39 Low Density Polyethylene - Blown Film Extrusion Riblene FC 39 is a high molecular weight low density polyethylene (LDPE) suitable for blown film extrusion. Riblene FC 39 is characterized by a high melt strength leading to a good bubble stability..
Film Tensile Strength at Break, TD	26.0 MPa	3770 psi	ASTM D882
NOVA Chemicals Novapol® 5% LF-0718-A in PF-0118-B LDPE Film Resin Improves gloss and reduces haze in blends with LLDPE, Improves melt strength and increases output in blends with LLDPEApplications: Blends with LLDPEAdditives: Base resinFilm properties are typical ..
Film Tensile Strength at Break, TD	26.0 MPa	3770 psi	ASTM D882
NOVA Chemicals Novapol® LF-0718-A LDPE Film Resin Improves gloss and reduces haze in blends with LLDPE, Improves melt strength and increases output in blends with LLDPEApplications: Blends with LLDPEAdditives: Base resinFilm properties are typical ..
Film Tensile Strength at Break, TD	26.0 MPa	3770 psi	ASTM D 882
NOVA Chemicals Novapol® TF-0438-E Hexene LMDPE Film Resin TF-0438-E complies with the U.S. FDA specifications for olefin polymers and may be used in the U.S. as an article or component of an article intended for use in contact with food, without temperatur..
Film Tensile Strength at Break, TD	26.0 MPa	3770 psi	ASTM D882
Petroquimica Triunfo Trithene® TS 7001 LDPE - Heavy Duty Low Friction Film The Trithene TS 7001 resin is a low-density polyethylene (LDPE) with high molecular weight, designed to satisfy those applications that require high mechanical strength and low coefficient of fricti..
Film Tensile Strength at Break, TD	26.0 MPa	3770 psi	ASTM D882
Petroquimica Triunfo Trithene® TX 7001 LDPE - High Molecular Weight The Trithene TX 7001 resin is a low-density polyethylene (LDPE) with high molecular weight, designed to satisfy those applications that require high mechanical strength and environmental stress crac..
Film Tensile Strength at Break, TD	26.0 MPa	3770 psi	ISO 527-3
Polimeri Europa Greenflex® FD 20 Ethylene Vinyl Acetate Copolymer - Blown Film Extrusion Greenflex FD 20 is an ethylene vinyl acetate copolymer (EVA) suitable for blown film extrusion. Films produced with Greenflex FD 20 exhibit good optical properties, high impact resistance, tensile ..
Film Tensile Strength at Break, TD	26.0 MPa	3770 psi	ASTM D882
Chevron Phillips HiD® 9662 HDPE Blown Film Resin (discontinued **) Resin Type: Linear Polyethylene HomopolymerCharacteristics: Unique Molecular Architecture Gives Outstanding Moisture Barrier Properties, Excellent Film Strength and Toughness for a Homopolymer, Give..
Film Tensile Strength at Break, TD	26.0 MPa	3770 psi	ASTM D882
NOVA Chemicals Novapol® PF-0118-B Butene LLDPE Film Resin Film Properties. Features: Toughness and strength.Applications: Trash bags, liners, general packaging.Data provided by the manufacturer.
Film Tensile Strength at Break, TD	26.0 MPa	3770 psi	ASTM D882
NOVA Chemicals Novapol® PF-0118-C Butene LLDPE Film Resin Film Properties. Features: Toughness and strength.Applications: Industrial liners, heavy duty bags.Data provided by the manufacturer.
Film Tensile Strength at Break, TD	26.0 MPa	3770 psi	ASTM D882
NOVA Chemicals Novapol® PF-0118-D Butene LLDPE Film Resin Film Properties. Features: Toughness and strength, thin films.Applications: Trash bags, garment film, bags-on-roll.Data provided by the manufacturer.
Film Tensile Strength at Break, TD	26.0 MPa	3770 psi	ASTM D882
NOVA Chemicals Novapol® PF-0118-F Butene LLDPE Film Resin Film Properties. Features: Toughness and strength.Applications: Stretch wrap, blend resin, industrial packaging.Data provided by the manufacturer.
Film Tensile Strength at Break, TD	26.0 MPa	3770 psi	ISO R527-1
Iran Petrochemical (PCC) 2100TN00 Low Density Polyethylene LDPE 2100TN00: Heavy duty film suitable for application in shrink hoods, industrial sacks, heavy duty carrier bags and liners.Information provided by Iran Petrochemical Commercial Co.
Film Tensile Strength at Break, TD	26.0 MPa	3770 psi	ASTM D882
SCG Chemicals EL-Proâ„¢ P600F Polypropylene Film Resin Key Characteristics:Good optical propertiesHigh productivityGood openability with 3000 ppm slip agent and 2700 ppm antiblocking agentRecommended Applications:Water quenched blown film for food and a..
Film Tensile Strength at Break, TD	26.0 MPa	3770 psi	ASTM D882
SCG Chemicals EL-Proâ„¢ P602F Polypropylene Film Resin Key Characteristics:Excellent optical propertiesHigh productivityRecommended Applications:Water quenched blown film for food and apparel packagingCan be blended with P600 for excellent clarityInform..
Film Tensile Strength at Break, TD	26.0 MPa	3770 psi	ISO 527-3
Borealis Borstar® FB3450 HDPE for Film Extrusion Borstar® FB3450 is a high density polyethylene. Borstar® FB3450 is well suited for multilayer coextruded films where higher stiffness and toughness than in standard LDPE and LLDPE is required. Ap..
Film Tensile Strength at Break, TD	26.0 MPa	3770 psi	ISO 527-3
Borealis FT3200 Low Density Polyethylene FT3200 is a Low Density Polyethylene for Film Extrusion. Applications heavy-duty bags, shrink film, construction films, and agricultural films. FT3200 contains no additives.Information provided by..
Film Tensile Strength at Break, TD	26.0 MPa	3770 psi	ISO 527-3
Total Lumicene® mPE M 4040 Metallocene Polyethylene, Cast Film Lumicene® mPE M 4040 is a Lumicene® metallocene based Polyethylene with hexene as comonomer.Lumicene® mPE M 4040 can be processed at high output rates with low extrusion pressure, low neck-in, ex..
Film Tensile Strength at Break, TD	26.0 MPa	3770 psi	ISO 527-3
Total PPR 6288 Random Copolymer Polypropylene, Cast Extrusion of Film Total Petrochemicals PPR 6288 is a random copolymer polypropylene with a melt flow index of 8 g/10 min for the cast extrusion of films with outstanding optical properties and easy heat weldability.P..
Film Tensile Strength at Break, TD	26.0 MPa	3770 psi	ASTM D882
Chevron Phillips MarFlex® 9659 HDPE Blown Film Resin Resin Type: Linear Polyethylene HomopolymerCharacteristics: Unique Molecular Architecture Gives Outstanding Moisture Barrier Properties, Excellent Film Strength and Toughness for a Homopolymer, Give..
Film Tensile Strength at Break, TD	26.0 MPa @Thickness 0.0250 mm	3770 psi @Thickness 0.000984 in	ASTM D882
Equate EFDA-7047 LLDPE Film Extrusion Resin EFDA-7047 is a linear low-density polyethylene resin for tubular blown film extrusion. Films made from this resin have good toughness, high tensile strength and puncture resistance. EFDA-7047 does n..
Film Tensile Strength at Break, TD	26.0 MPa @Thickness 0.0250 mm	3770 psi @Thickness 0.000984 in	ASTM D882
Equate EFDC-7087 LLDPE Film Extrusion Resin EFDC-7087 is a linear low-density polyethylene resin for tubular blown film extrusion. Films made from EFDC-7087 have good toughness, high tensile strength and outstanding puncture resistance. EFDC-..
Film Tensile Strength at Break, TD	26.0 MPa	3770 psi	ASTM D882
Huntsman Rexell® M3109 Blown Film Extrusion LLDPE (discontinued **) Linear-low medium density copolymer and FDA compliant.Features: Excellent combination of stiffness, heat resistance, and impermeability to water vapor.Applications: Food packaging, multi-layer syste..