Eastman Eastar GN102 Copolyester (discontinued **)

Category	Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), Unreinforced
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Eastman Eastar GN102 Copolyester (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Eastar GN102 copolyester is a glycol modified polyethylene terephthalate (PET) that contains an ultraviolet inhibitor and mold release. Eastar GN102 copolyester will not crystallize and thus offers wider processing latitude than conventional crystallizable polyesters. This material offers an excellent combination of clarity, toughness, and melt strength that makes it useful for a variety of processing techniques and end-use applications.Applications/UsesLighting

Physical Properties	Metric	English	Comments
Specific Gravity	1.27 g/cc	1.27 g/cc	ASTM D792

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	117	117	ASTM D785
Tensile Strength at Break	26.0 MPa	3770 psi	ASTM D638
Tensile Strength, Yield	51.0 MPa	7400 psi	ASTM D638
Elongation at Break	72 %	72 %	ASTM D638
Elongation at Yield	4.0 %	4.0 %	ASTM D638
Flexural Strength	72.0 MPa	10400 psi	ASTM D790
Flexural Modulus	2.10 GPa	305 ksi	ASTM D790
Izod Impact, Notched	0.480 J/cm @Temperature 23.0 °C	0.899 ft-lb/in @Temperature 73.4 °F	ASTM D256
	0.530 J/cm @Temperature -40.0 °C	0.993 ft-lb/in @Temperature -40.0 °F	ASTM D256
Izod Impact, Unnotched	NB	NB	ASTM D4812
	NB @Temperature -40.0 °C	NB @Temperature -40.0 °F	ASTM D4812

Processing Properties	Metric	English	Comments
Melt Temperature	210 - 270 °C	410 - 518 °F	Extrusion
	250 - 270 °C	482 - 518 °F	Injection Molding
Mold Temperature	15.0 - 40.0 °C	59.0 - 104 °F
Drying Temperature	70.0 °C	158 °F
Dry Time	6 hour	6 hour