Eastman Eastalloy DA107 PC+PET Copolyester/Polycarbonate  (discontinued **)

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/PET Polyester Blend , Polyester, TP , Polyethylene Terephthalate (PET)
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eastman Eastalloy DA107 PC+PET Copolyester/Polycarbonate  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
ISO data as provided by the manufacturer, Eastman Chemical
Physical Properties Metric English Comments
Density 1.21 g/cc
0.0437 lb/in³
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
Mechanical Properties Metric English Comments
Tensile Strength, Yield 44.0 MPa
6380 psi
50 mm/min
Elongation at Break >= 50 %
>= 50 %
Elongation at Yield 4.5 %
4.5 %
Tensile Modulus 1.84 GPa
267 ksi
1mm/min
Charpy Impact Unnotched NB
NB
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
Charpy Impact, Notched 9.00 J/cm²
42.8 ft-lb/in²
Partial Break
1.15 J/cm²

@Temperature -30.0 °C
 5.47 ft-lb/in²

@Temperature -22.0 °F
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 62.0 µm/m-°C

@Temperature 20.0 °C
 34.4 µin/in-°F

@Temperature 68.0 °F
CTE, linear, Transverse to Flow 71.0 µm/m-°C

@Temperature 20.0 °C
 39.4 µin/in-°F

@Temperature 68.0 °F
Melting Point 220 °C
428 °F
Deflection Temperature at 0.46 MPa (66 psi) 86.0 °C
187 °F
Deflection Temperature at 1.8 MPa (264 psi) 74.0 °C
165 °F
Vicat Softening Point 90.0 °C
194 °F
Glass Transition Temp, Tg 92.0 °C
198 °F
Processing Properties Metric English Comments
Melt Temperature 260 - 280 °C
500 - 536 °F