E-Polymers Tekaloy® G70A4 Impact Resistance at Low Temperature PC/ABS Alloy
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | E-Polymers Co. Ltd. |
| Trade Name | TEKALOY® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | E-Polymers Tekaloy® G70A4 Impact Resistance at Low Temperature PC/ABS Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Impact Resistance at Low TemperatureInformation provided by E-Polymers Co. Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | |
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 250 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 111 | 111 | ASTM D785 |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ASTM D638 |
| Elongation at Break | >= 100 % | >= 100 % | ASTM D638 |
| Flexural Yield Strength | 78.0 MPa | 11300 psi | ASTM D790 |
| Flexural Modulus | 2.15 GPa | 312 ksi | ASTM D790 |
| Izod Impact, Notched | 6.50 J/cm | 12.2 ft-lb/in | ASTM D256 |
| 5.50 J/cm @Temperature -30.0 °C |
10.3 ft-lb/in @Temperature -22.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 113 °C | 235 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 220 - 290 °C | 428 - 554 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F |
Users viewing this material also viewed the following:
- MV Labs BA800 BaC2O4 Barium oxalate
- Nilit FRIANYL A63 W-GV30 Nylon 6.6, std. viscosity for injection molding, 30% glass fiber reinforced
- Polymer Resources TPSF-FR1 PBT, 30% Glass Reinforced Structural Foam Grade, Flame Retardant
- LATI Latishield 66-08A G/25-V0KB1 PA66, Steel/Glass Fiber Reinforced, Flame Retardant
- Saint-Gobain CHR® HM650 High Modulus PTFE Film Backing Silicone Adhesive Pressure Sensitive Tape
- EMS-Grivory Grivory® XE 4108 nat PA612-GF50
- Axiall 8740 Moldings & Extrusions Flexible PVC
- RheTech Products HP506-01B 22% Talc Reinforced High Performance Polypropylene, UV Stabilized, Black
Copyright © lookpolymers.com All Rights Reserved