Dow Elite® 5400 Linear Low Density Polyethylene

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer Dow Chemical
Trade Name Elite®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow Elite® 5400 Linear Low Density Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
5400 enhanced polyethylene resin is a copolymer produced via INSITE technology from Dow Plastics. It offers extremely high impact resistance, combined with excellent tear, tensile, and optical properties for high strength blown film applications. In addition, 5400 resin offers a unique combination of low temperature seal initiation, higher modulus, and low blocking tendencies for automated packaging applications. It complies with U.S. FDA regulation 21 CFR 177.1520 c 3.2 (a) when used unmodified and processed according to good manufacturing practices. For food contact compliance statements, your nearest Dow office should be contacted.Data provided by Dow Chemical.
Physical Properties Metric English Comments
Density 0.916 g/cc
0.0331 lb/in³
Melt Flow 1.0 g/10 min

@Load 2.16 kg
1.0 g/10 min

@Load 4.76 lb
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 11.3 MPa
1640 psi
Film Tensile Strength at Yield, TD 11.2 MPa
1620 psi
Film Elongation at Break, MD 635 %
635 %
Film Elongation at Break, TD 662 %
662 %
Secant Modulus, MD 0.171 GPa
24.8 ksi
Film value
Secant Modulus, TD 0.1825 GPa
26.47 ksi
Film value
Elmendorf Tear Strength MD 630 g
630 g
Unspecified film thickness
Elmendorf Tear Strength TD 770 g
770 g
Unspecified film thickness
Dart Drop Test >= 830 g
>= 1.83 lb
Film Tensile Strength at Break, MD 53.9 MPa
7820 psi
Film Tensile Strength at Break, TD 51.7 MPa
7500 psi
Thermal Properties Metric English Comments
Vicat Softening Point 102 °C
216 °F
Optical Properties Metric English Comments
Haze 9.5 %
9.5 %
Processing Properties Metric English Comments
Processing Temperature 90.0 °C
194 °F
Seal Initiation temperature