- Chi Mei Wonderloy® PC-175D PC/ABS Alloy (discontinued **)
Chi Mei Wonderloy® PC-175D PC/ABS Alloy (discontinued **)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chi Mei Wonderloy® PC-175D PC/ABS Alloy
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Optical Disk
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Melt Flow | 50 g/10 min @Load 1.20 kg, Temperature 300 °C |
50 g/10 min @Load 2.65 lb, Temperature 572 °F |
Melt Volume Rate (ml/10 min); ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 104 MPa | 15100 psi | H358/30; ISO 2039-1 |
| Tensile Strength at Break | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 65 % | 65 % | 50 mm/min; ISO 527 |
| Flexural Strength | 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | ISO 180/4A |
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | annealed; ISO 75 |
| 140 °C | 284 °F | unannealed; ISO 75 | |
| Vicat Softening Point | 142 °C @Load 5.00 kg |
288 °F @Load 11.0 lb |
50°C/hr; ISO 306 |
| 147 °C @Load 1.00 kg |
297 °F @Load 2.20 lb |
50°C/hr; ISO 306 |
Users viewing this material also viewed the following:
- 5265 Polyurethane-based Biomedical Elastomer
- Chevron Phillips HiD® 9396T HDPE Natural Pipe Resin (discontinued **)
- Hexion Bakelite™ MP 4165 Melamine Phenolic Resin, Copper Adhesive, Low Shrinkage, High Mechanical Strength (d
- Flint Hills P4G2Z-026 Homopolymer Polypropylene
- Momentive Performance Materials HV 3/506 Heat Cured Rubber - High Temperature
- Teknor Apex MONPRENE® MP 1900 Thermoplastic Elastomer
- SCG Chemicals EL-Proâ„¢ P403J Polypropylene Injection Molding
- A. Schulman POLYBATCH™ Green 3315 Concentrate Based In Polyethylene
- Westlake EMAC® Plus SP1307 20% Ethylene-Methyl Acrylate Copolymer
- PolyOne Synprene® RT-3830M Thermoplastic Elastomer - SBC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved