Chi Mei Kibisan® PN137H SAN Resin, General Purpose

Category Polymer , Thermoplastic , SAN Polymer , Styrene Acrylonitrile (SAN), Molded
Manufacturer Chi Mei Corporation (ChiMei)
Trade Name Kibisan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chi Mei Kibisan® PN137H SAN Resin, General Purpose.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Calsak Corporation
Physical Properties Metric English Comments
Specific Gravity 1.06 g/cc
1.06 g/cc
ASTM D792
Melt Flow 0.90 g/10 min

@Load 5.00 kg,
Temperature 200 °C
 0.90 g/10 min

@Load 11.0 lb,
Temperature 392 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell M 86

@Thickness 6.35 mm
 86

@Thickness 0.250 in
 ASTM D788
Tensile Strength, Yield 78.74 MPa

@Thickness 3.17 mm
 11420 psi

@Thickness 0.125 in
 6 mm/min; ASTM D638
Elongation at Yield 5.0 %

@Thickness 3.17 mm
 5.0 %

@Thickness 0.125 in
 6 mm/min; ASTM D638
Flexural Yield Strength 112.5 MPa

@Thickness 6.35 mm
 16310 psi

@Thickness 0.250 in
 2.8 mm/min; ASTM D790
Flexural Modulus 3.79 GPa

@Thickness 6.35 mm
 550 ksi

@Thickness 0.250 in
 2.8 mm/min; ASTM D790
Izod Impact, Notched 0.187 J/cm

@Thickness 6.35 mm,
Temperature 23.0 °C
 0.350 ft-lb/in

@Thickness 0.250 in,
Temperature 73.4 °F
 ASTM D256
0.224 J/cm

@Thickness 3.17 mm,
Temperature 23.0 °C
 0.420 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 95.0 °C

@Thickness 6.35 mm
 203 °F

@Thickness 0.250 in
 unannealed, 120°C/hr; ASTM D648
104 °C

@Thickness 6.35 mm
 219 °F

@Thickness 0.250 in
 annealed, 120°C/hr; ASTM D648
Vicat Softening Point 110 °C

@Thickness 3.17 mm
 230 °F

@Thickness 0.125 in
 50°C/hr; ASTM D1525
Flammability, UL94 HB

@Thickness 1.59 mm
 HB

@Thickness 0.0625 in