Chevron Phillips Marlex® CL-200YNR JN (Natural) Rotational molding crosslinkable high density polyethylene  (d

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Crosslinkable
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chevron Phillips Marlex® CL-200YNR JN (Natural) Rotational molding crosslinkable high density polyethylene  (d.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Benefits: crosslinks during molding - has outstanding melt strength at 204°C, is formulated to provide maximum UV protection for long-term outdoor weathering, contains an internal mold release, excellent stress cracking resistance to gasoline and other chemicals, outstanding impact strength at temperatures as low as -40°CCharacteristics: 100 J at 3 mm Impact Strength (-40°C); ARM Test Method, 260 J at 6 mm Impact Strength (-40°C); ARM Test MethodApplications: industrial and agricultural chemical storage tanks, small engine, snowmobile, and marine fuel tanks, seatsInformation provided by Chevron Phillips Chemical Company
Physical Properties Metric English Comments
Density 0.941 g/cc
0.0340 lb/in³
ASTM D1505
Environmental Stress Crack Resistance >= 1000 hour

@Temperature 50.0 °C
>= 1000 hour

@Temperature 122 °F
Condition A; ASTM D 1693
Mechanical Properties Metric English Comments
Tensile Strength, Yield 18.0 MPa
2610 psi
ASTM D638 Type IV
Elongation at Break 450 %
450 %
ASTM D638 Type IV
Flexural Modulus 0.690 GPa
100 ksi
ASTM D790
Thermal Properties Metric English Comments
Vicat Softening Point 124 °C
255 °F
ASTM D1525
Brittleness Temperature <= -90.0 °C
<= -130 °F
ASTM D746
Processing Properties Metric English Comments
Processing Temperature 246 - 326 °C
475 - 619 °F
oven temperature for hot air machines 246-326°C, marlex crosslinkable resins require special handling during processing