Chevron Phillips HiD® 9606 HDPE Blown Film and Sheet  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chevron Phillips HiD® 9606 HDPE Blown Film and Sheet  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Resin Type: ASTM D 4976 Classification: PE 235, A 54502Applications:General Purpose Films and Sheet, Coextruded Film Structures, Deli and Tissue Films, Sheet Thermoforming Applications with Good Stress Crack ResistanceFilm properties below based on film thickness of 25.4 µm.Data provided by Chevron Chemical.
Physical Properties Metric English Comments
Density 0.951 g/cc
0.0344 lb/in³
ASTM D1505
Melt Flow 0.26 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.26 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D 1238
High Load Melt Index 30 g/10 min

@Load 21.6 kg,
Temperature 190 °C
30 g/10 min

@Load 47.6 lb,
Temperature 374 °F
High Load Melt Index; ASTM D 1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 530 %
530 %
ASTM D882
Film Elongation at Break, TD 400 %
400 %
ASTM D882
Secant Modulus, MD 0.750 GPa
109 ksi
ASTM D882
Secant Modulus, TD 0.910 GPa
132 ksi
ASTM D882
Elmendorf Tear Strength, MD 0.394 g/micron
10.0 g/mil
Notched; ASTM D1922
Elmendorf Tear Strength, TD 4.33 g/micron
110 g/mil
ASTM D1922
Dart Drop <= 1.20 g/micron
<= 30.5 g/mil
F<sub>50</sub>; 1.5 in. dart/26 in. drop height; ASTM D 1709
Film Tensile Strength at Break, MD 28.0 MPa
4060 psi
ASTM D882
Film Tensile Strength at Break, TD 21.0 MPa
3050 psi
ASTM D882
Thermal Properties Metric English Comments
Vicat Softening Point 126 °C
259 °F
ASTM D1525
Processing Properties Metric English Comments
Melt Temperature 221 °C
430 °F