Borealis BorPure™ RD234CF Polypropylene Random Copolymer

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer
Manufacturer Borealis
Trade Name BorPURE™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis BorPure™ RD234CF Polypropylene Random Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
BorPure™ RD234CF is a random copolymer. This grade is suitable for the manufacturing of unoriented films on chill roll processes. Applications: RD234CF is recommended for food packaging, stationary films, lamination films, textile packaging film, and medical applications.Information provided by Borealis AG
Physical Properties Metric English Comments
Density 0.900 - 0.910 g/cc
0.0325 - 0.0329 lb/in³
base resin; ISO 1183
Melt Flow 8.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
8.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Antiblock Level 1800 ppm
1800 ppm
SiO<sub>2</sub>; Borealis Method
Slip Level 2000 ppm
2000 ppm
EAA; Borealis Method
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 550 - 750 %
550 - 750 %
ISO 527-3
Film Elongation at Break, TD 550 - 750 %
550 - 750 %
ISO 527-3
Tensile Modulus 0.500 - 0.600 GPa
72.5 - 87.0 ksi
MD/TD; ISO 527-3
Flexural Modulus 1.00 GPa
145 ksi
ISO 178
Dart Drop, Total Energy 17.0 J

@Thickness 0.0500 mm
12.5 ft-lb

@Thickness 0.00197 in
1100N; ISO 7765-2
Coefficient of Friction 0.20 - 0.30
0.20 - 0.30
film/film; ISO 8295
Film Tensile Strength at Break, MD 30.0 - 50.0 MPa
4350 - 7250 psi
ISO 527-3
Film Tensile Strength at Break, TD 25.0 - 45.0 MPa
3630 - 6530 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 148 - 154 °C
298 - 309 °F
DSC; ISO 3146
Vicat Softening Point 139 °C

@Load 1.02 kg
282 °F

@Load 2.25 lb
A50; ISO 306
Optical Properties Metric English Comments
Haze <= 2.0 %
<= 2.0 %
ASTM D1003
Gloss >= 120 %
>= 120 %
20° of arc; ASTM D2457