- Barlog Plastics KEBATER A0230 PBT/ABS, 30% glass fiber reinforced, low warpage
Barlog Plastics KEBATER A0230 PBT/ABS, 30% glass fiber reinforced, low warpage
| Category | Polymer , Thermoplastic , ABS Polymer , ABS/Polyester Alloy + GF , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | Barlog Plastics |
| Trade Name | KEBATER |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Barlog Plastics KEBATER A0230 PBT/ABS, 30% glass fiber reinforced, low warpage.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
(PBT+ABS)-GF30Information provided by BARLOG plastics GmbH.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527-1 |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527-1 |
| Tensile Modulus | 8.50 GPa | 1230 ksi | ISO 527-1 |
| Charpy Impact Unnotched | 4.50 J/cm² | 21.4 ft-lb/in² | ISO 179-1eU |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+11 ohm | 1.00e+11 ohm | IEC 60093 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Resin Type | (PBT+ABS)-GF30 |
Users viewing this material also viewed the following:
- Quadrant EPP Duratron® PAI T4203 PAI, unfilled, extruded (ISO Data)
- SABIC Innovative Plastics LNP FARADEX DX92079 PC (Europe-Africa-Middle East)
- Eastman 1830A Polyethylene (discontinued **)
- Haynes 242® alloy, after 8000 hours exposure at 650°C (1200°F)
- Silberline Silvet® 860-20-P
- SABIC Innovative Plastics NORYL PKN4752 PPE+PS (Asia Pacific)
- A. Schulman CP851 High Flow, Injection Molding Grade
- AKG Polymers Vision PP PPH BL5003 Polypropylene Homopolymer Compound
- 3M Scotch® 77 White Fire-Retardant Electric Arc Proofing Tape
- 3A Composites Core Materials AIREX® R63.140 Damage Tolerant Foam
Copyright © lookpolymers.com All Rights Reserved