Equate EMDA-6147 HDPE Blow Molding Resin

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade
Manufacturer Equate
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Equate EMDA-6147 HDPE Blow Molding Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
EMDA-6147 is a high density polyethylene copolymer resin designed for blow molding of large size containers. Its high molecular weight and broad molecular weight distribution with a balanced density provide excellent mold-ability, toughness and stress-cracking resistance. The molded articles exhibit good surface attributes.Applications: EMDA-6147 is suitable for blow molding of closed head shipping containers of up to 50 liter size, fuel tanks, drums, jerry cans and other similar parts. The molded parts have smooth surfaces that can be readily treated for high quality printing. The containers may be utilized for packaging a variety of aggressive materials such as industrial chemicals, latex paint, printing inks and adhesives. Food can also be packaged in the containers in line with conformity of the resin with food contact regulations. EMDA-6147 is also suitable for making non-pressure “gravity” pipes for drainage and sewage applicationsInformation provided by Equate
Physical Properties Metric English Comments
Density 0.952 g/cc
0.0344 lb/in³
ASTM D792
ESCR 100% Igepal® 1000 hour

@Temperature 50.0 °C
1000 hour

@Temperature 122 °F
ASTM D1693 B
Melt Flow 0.070 g/10 min

@Load 2.16 kg
0.070 g/10 min

@Load 4.76 lb
ASTM D1238
High Load Melt Index 9.0 g/10 min

@Load 21.6 kg
9.0 g/10 min

@Load 47.6 lb
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 35.0 MPa
5080 psi
ASTM D638
Tensile Strength, Yield 26.0 MPa
3770 psi
ASTM D638
Elongation at Break >= 750 %
>= 750 %
ASTM D638
Flexural Modulus 1.18 GPa
171 ksi
ASTM D790
Izod Impact, Unnotched (ISO) 17.0 kJ/m²
8.09 ft-lb/in²
ASTM D256
Thermal Properties Metric English Comments
Melting Point 131 °C
268 °F
Equate Test Method
Crystallization Temperature 116 °C
241 °F
Equate Test Method
Vicat Softening Point 125 °C
257 °F
ASTM D1525
Processing Properties Metric English Comments
Zone 1 204 °C
399 °F
Zone 2 204 °C
399 °F
Zone 3 204 °C
399 °F
Zone 4 204 °C
399 °F
Die Temperature 204 °C
399 °F
Melt Temperature 210 °C
410 °F
Head Temperature 204 °C
399 °F