BCC Products BC 9020 Silicone RTV Rubber

Category Polymer , Adhesive , Thermoset , Silicone , Silicone, RTV, Adhesive/Sealant Grade
Manufacturer BCC Products
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BCC Products BC 9020 Silicone RTV Rubber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
BC 9020 is a violet colored, two-component, flowable compound that regardless of thickness or confinement, cures at room temperature. The cured rubber is high strength and high tear with good elongation. In addition, BC9020 features low viscosity, low durometer and resistance to sulfur clays. Application: BC 9020 is a mold making material designed for the manufacture of flexible molds. These rubber molds are recommended for the use in repetitive production of intricate shapes cast from epoxy or urethane resins. These molds are also used in the potting of electronic components and in protecting sensitive assemblies against thermal shock and vibration. Temperatures above 80º F in the modeling and encapsulating area should be avoided to prevent premature expiration of pot life. BC9020 should be thoroughly stirred before mixing, since pigments settle during storage. Mixing containers should be clean and dry before use and then should be filled to 1/4 capacity to allow room for mixing and deaeration. It is recommended that separate tools be used for mixing the catalyst and the compound to avoid cross contamination. When mixing by hand, material clinging to sides and bottom should be folded into main contents twice. When mixing is done with a power mixer, two fifteensecond cycles are generally sufficient for thorough mixing. Avoid prolonged mixing at high speeds as this will generate heat and decrease the pot life of the material. Deaeration: Air entrapped during the mixing cycle must be removed to eliminate voids in the cured compound. Place the mixture in a vacuum of 29 inches of mercury. The mixture will expand to `3-5 times its original volume, crest and recede approximately to its original level. Continue the deaeration for an additional 1-2 minutes and the material will be ready to use.Information provided by BCC Products, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.10 g/cc
1.10 g/cc
Brookfield Viscosity 10000 cP
10000 cP
Catalyst
3.10e+6 cP
3.10e+6 cP
Mixed
7.00e+6 cP

@Temperature 25.0 °C
7.00e+6 cP

@Temperature 77.0 °F
Compound
Linear Mold Shrinkage 0.0030 - 0.0040 cm/cm
0.0030 - 0.0040 in/in
Mechanical Properties Metric English Comments
Hardness, Shore A 20 - 25
20 - 25
Tensile Strength, Ultimate 4.14 MPa
600 psi
Elongation at Break 500 %
500 %
Tear Strength 21.0 kN/m
120 pli
Thermal Properties Metric English Comments
Heat Distortion Temperature 232 °C
450 °F
estimate
Processing Properties Metric English Comments
Cure Time 480 min

@Temperature 24.0 °C
8.00 hour

@Temperature 75.2 °F
handling time
1440 min

@Temperature 24.0 °C
24.0 hour

@Temperature 75.2 °F
90% cure
2880 min

@Temperature 24.0 °C
48.0 hour

@Temperature 75.2 °F
full cure
Pot Life 60 min

@Temperature 25.0 °C
60 min

@Temperature 77.0 °F
Shelf Life 6.00 Month
6.00 Month
Descriptive Properties Value Comments
Mix Ratio 10:1 by weight