- Arkema Group Orgalloy® RS 6015 EST Nylon 6 Alloy, 18% Glass Fiber (Conditioned)
Arkema Group Orgalloy® RS 6015 EST Nylon 6 Alloy, 18% Glass Fiber (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled |
| Manufacturer | Arkema |
| Trade Name | Orgalloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Orgalloy® RS 6015 EST Nylon 6 Alloy, 18% Glass Fiber (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
RS 60 series, rigid polyamide 6 alloy: easy to process, chemical resistance (no known solvents) and low moisture absorption leading to stability of mechanical, electrical and dimensional properties.RS 6015EST: 18% glass fiber, for blow molding of technical parts under the hood (air intake), high temperature resistance.ISO data provided by the manufacturer, Arkema.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | |
| Water Absorption | 2.8 % | 2.8 % | |
| Moisture Absorption at Equilibrium | 1.1 % | 1.1 % | Humidity Absorption |
| Melt Flow | 1.3 g/10 min @Load 2.16 kg, Temperature 235 °C |
1.3 g/10 min @Load 4.76 lb, Temperature 455 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 110 MPa | 16000 psi | 5 mm/min |
| Elongation at Break | 3.5 % | 3.5 % | 5 mm/min |
| Tensile Modulus | 3.50 GPa | 508 ksi | 1 mm/min |
| Charpy Impact, Notched | 1.10 J/cm² | 5.24 ft-lb/in² | |
| 0.700 J/cm² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
||
| Tensile Creep Modulus, 1 hour | 2700 MPa | 392000 psi | |
| Tensile Creep Modulus, 1000 hours | 1920 MPa | 278000 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10°C/min |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 175 °C | 347 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
| Dielectric Constant | 2.6 @Frequency 100 Hz |
2.6 @Frequency 100 Hz |
|
| 3.3 @Frequency 1e+6 Hz |
3.3 @Frequency 1e+6 Hz |
||
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | |
| Dissipation Factor | 0.024 @Frequency 1e+6 Hz |
0.024 @Frequency 1e+6 Hz |
|
| 0.063 @Frequency 100 Hz |
0.063 @Frequency 100 Hz |
||
| Comparative Tracking Index | 600 V | 600 V |