Abatron AboCast 8-15/Abocure 8-15 Epoxy (discontinued **)

Category	Polymer , Thermoset , Epoxy
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Abatron AboCast 8-15/Abocure 8-15 Epoxy (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

2-part, clear, solvent-free dielectric epoxy casting compound.Processing: 100/11.80 ratio (pbw); Gel time, 100 g (3.5 oz.): 70 minutes; cures in 16 hours at 25°C (77°F); postcure: 2 hours at 100°C (212°F).Applications: solventless casting, adhesive, and coating.

Physical Properties	Metric	English	Comments
Water Absorption	0.15 %	0.15 %	in 24 hours.
Viscosity Measurement	400.01	400.01

Mechanical Properties	Metric	English
Hardness, Shore D	86	86
Tensile Strength, Ultimate	50.33 MPa	7300 psi
Elongation at Break	5.8 %	5.8 %
Modulus of Elasticity	2.965 GPa	430.0 ksi
Flexural Yield Strength	121.35 MPa	17600 psi
Izod Impact, Notched	0.235 J/cm	0.440 ft-lb/in

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	79.0 °C	174 °F	Deflection temperature; load unknown.

Electrical Properties	Metric	English
Electrical Resistivity	2.40e+11 ohm-cm @Temperature 93.3 °C	2.40e+11 ohm-cm @Temperature 200 °F
	1.50e+13 ohm-cm @Temperature 65.6 °C	1.50e+13 ohm-cm @Temperature 150 °F
	5.90e+13 ohm-cm @Temperature 25.0 °C	5.90e+13 ohm-cm @Temperature 77.0 °F
Dielectric Constant	3.84 @Frequency 1e+6 Hz	3.84 @Frequency 1e+6 Hz
Dissipation Factor	0.030 @Frequency 1e+6 Hz	0.030 @Frequency 1e+6 Hz

Processing Properties	Metric	English	Comments
Processing Temperature	25.0 °C	77.0 °F	Curing time: 16 hours; Postcure: 2 hours/100°C (212°F)