Polymer Property : Processing Temperature = 25.0 °C Product List

Processing Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Processing Properties Metric English Comments
Processing Temperature 25.0 °C
77.0 °F
Curing Agent Temperature
Northstar Polymers MSS-A90A High Performance Polyurethane Cast Elastomer System 90A
This is a Ester/MDI base high-performance polyurethane casting system. This systems is recommended to applications in which the part requires high tensile strength, cut/tear resistance, dry-abrasio..
Processing Temperature 25.0 - 125 °C
77.0 - 257 °F
Average value: 36.2 °C Grade Count:53
Overview of materials for Silicone, RTV, Adhesive/Sealant Grade
This property data is a summary of similar materials in the MatWeb database for the category "Silicone, RTV, Adhesive/Sealant Grade". Each property range of values reported is minimum and maximum va..
Processing Temperature 25.0 °C
77.0 °F
Curing time: 16 hours; Postcure: 2 hours/100°C (212°F)
Abatron AboCast 8-8/Abocure 8-8 Epoxy  (discontinued **)
2-part solvent-free dielectric epoxy casting compound.Processing: 100/50 ratio (pbw); Gel time, 1 lb. (2.2 kg): 135 minutes; cures in 16 hours at 25°C (77°F); postcure: 2 hours at 100°C (212°F)...
Processing Temperature 25.0 °C
77.0 °F
Curing time: 16 hours; Postcure: 2 hours/100°C (212°F)
Abatron AboCast 8-13/Abocure 8-13 Epoxy  (discontinued **)
2-part, clear, solvent-free dielectric epoxy casting compound.Processing: 100/12.80 ratio (pbw); Gel time, 100 g (3.5 oz.): 53 minutes; cures in 16 hours at 25°C (77°F); postcure: 2 hours at 100°..
Processing Temperature 25.0 °C
77.0 °F
Cure Schedule: 7 days @ 25°C
Huntsman HY 3440 Phenalkamine Hardener
Approx. H+ equivalent weight 80. Mix Ratio with GY 6010 is 30.Comments/Applications: Low temperature cure coatings with excellent corrosion and moisture resistance. Cure can go down to 0°C. F..
Processing Temperature 25.0 °C
77.0 °F
Momentive Performance Materials RTV109 Aluminum Adhesive Sealant, High Strength Paste
One-part acetoxy cure. Acetoxy cure silicones are the most commonly used type of RTV materials and are considered GE Silicones' general purpose product line. Typical uses: High strength high perfo..
Processing Temperature 25.0 °C
77.0 °F
Momentive Performance Materials RTV128 Translucent Adhesive Sealant, General Purpose Paste
One-part modified alkoxy cure. Modified alkoxy materials cure at room temperature and will outgas a small amount of ammonia and some alcohol during cure. Typical uses: General purpose for bonding ..
Processing Temperature 25.0 °C
77.0 °F
Momentive Performance Materials RTV162 White Adhesive Sealant, Non-Corrosive Paste
One-part totally non-corrosive alkoxy cure. Alkoxy cure silicones are neutral cure materials that offer exceptional adhesion and are non-corrosive to most metals. Typical uses: Non-corrosive bindi..
Processing Temperature 25.0 °C
77.0 °F
Momentive Performance Materials RTV167 Gray Adhesive Sealant, Non-Corrosive High Strength
One-part totally non-corrosive alkoxy cure. Alkoxy cure silicones are neutral cure materials that offer exceptional adhesion and are non-corrosive to most metals. Typical uses: Highest strength ad..
Processing Temperature 25.0 °C
77.0 °F
Cure time 24 hrs.
Momentive Performance Materials RTV41 White General Purpose Potting/Encapsulating Compound
Two-part condensation cure. Two-part condensation cure silicones RTVs are designed to cute at room temperature, and can be applied at temperature up to one inch (2.5 cm). These are very tough mate..
Processing Temperature 25.0 °C
77.0 °F
Momentive Performance Materials RTV5223 Black Adhesive Sealant, Low Modulus Paste
One-part totally non-corrosive alkoxy cure. Alkoxy cure silicones are neutral cure materials that offer exceptional adhesion and are non-corrosive to most metals. Typical uses: Economical true neu..
Processing Temperature 25.0 °C
77.0 °F
Momentive Performance Materials RTV6802 White Adhesive Sealant, Industrial Plastic Adhesive
One-part modified alkoxy cure. Modified alkoxy materials cure at room temperature and will outgas a small amount of ammonia and some alcohol during cure. Typical uses: Primerless adhesion to many ..
Processing Temperature 25.0 °C
77.0 °F
Cure time 24 hrs.
Momentive Performance Materials RTV8112 White General Purpose Potting/Encapsulating Compound
Two-part condensation cure. Two-part condensation cure silicones RTVs are designed to cute at room temperature, and can be applied at temperature up to one inch (2.5 cm). These are very tough mate..
Processing Temperature 25.0 °C
77.0 °F
Cure time 8 hours.
Momentive Performance Materials TSE3331 Dark Gray Thermally Conductive Potting/Encapsulating Compound
Two-part addition cure. Two-part addition cure RTV silicones can be cured very quickly with the use of high heat. Addition cure products have no cure by-products and can be used to unlimited depth..
Processing Temperature 25.0 °C
77.0 °F
Momentive Performance Materials TSE397 Translucent Adhesive Sealant, Semi-Flowable
One-part totally non-corrosive alkoxy cure. Alkoxy cure silicones are neutral cure materials that offer exceptional adhesion and are non-corrosive to most metals. Typical uses: Non-corrosive adhes..
Processing Temperature 25.0 °C
77.0 °F
Momentive Performance Materials FRV1106 Red Fluorosilicone Adhesive Sealant, Fuel Resistant Paste
One-part acetoxy cure. Alkoxy cure silicones are neutral cure materials that offer exceptional adhesion and are non-corrosive to most metals. Typical uses: For use in contact with fuel, solvents, ..
Processing Temperature 25.0 °C
77.0 °F
Cure time to 0.125 in. is 2 hours
Momentive Performance Materials IGS3719-D1 Insulating Glass Sealant, Gray
One-component silicone which cures to form a high strength, high modulus sealant with excellent adhesion to glass. Cure Method: Alkoxy (Neutral). Tack-free time 0.5 hr. Peel Strength 50 lb/in. ..
Processing Temperature 25.0 °C
77.0 °F
Momentive Performance Materials IS802 White Adhesive Sealant, General Purpose Paste
One-part acetoxy cure. Acetoxy cure silicones are the most commonly used type of RTV materials and are considered GE Silicones' general purpose product line. Typical uses: Use for general purpose,..
Processing Temperature 25.0 °C
77.0 °F
Momentive Performance Materials IS806 Red Adhesive Sealant, General Purpose Paste
One-part alkoxy cure. Typical uses: High-heat applications; encapsulate and seal heating elements.Data provided by the manufacturer, GE Silicones.GE Silicones became a part of Momentive Performance..
Processing Temperature 25.0 °C
77.0 °F
Cure time 24 hrs.
Momentive Performance Materials RTV511 White Extreme Low Temperature Potting/Encapsulating Compound
Two-part condensation cure. Two-part condensation cure silicones RTVs are designed to cute at room temperature, and can be applied at temperature up to one inch (2.5 cm). These are very tough mate..
Processing Temperature 25.0 °C
77.0 °F
Cure time 24 hrs.
Momentive Performance Materials RTV560 Red Extreme High Temperature Potting/Encapsulating Compound
Two-part condensation cure. Two-part condensation cure silicones RTVs are designed to cute at room temperature, and can be applied at temperature up to one inch (2.5 cm). These are very tough mate..
Processing Temperature 25.0 °C
77.0 °F
Cure time 7 days.
Momentive Performance Materials RTV567 Translucent Extreme Low Temperature Potting/Encapsulating Compound
Two-part condensation cure. Two-part condensation cure silicones RTVs are designed to cute at room temperature, and can be applied at temperature up to one inch (2.5 cm). These are very tough mate..
Processing Temperature 25.0 °C
77.0 °F
Cure time 24 hrs.
Momentive Performance Materials RTV60 Red Extreme High Temperature Potting/Encapsulating Compound
Two-part condensation cure. Two-part condensation cure silicones RTVs are designed to cute at room temperature, and can be applied at temperature up to one inch (2.5 cm). These are very tough mate..
Processing Temperature 25.0 °C
77.0 °F
Cure time 30 min.
Momentive Performance Materials RTV6136 Potting/Encapsulating Gel
Two-part addition cure. Two-part addition cure RTV silicones can be cured very quickly with the use of high heat. Addition cure products have no cure by-products and can be used to unlimited depth..
Processing Temperature 25.0 °C
77.0 °F
Momentive Performance Materials RTV6703 Black Adhesive Sealant, General Purpose Paste
One-part modified alkoxy cure. Modified alkoxy materials cure at room temperature and will outgas a small amount of ammonia and some alcohol during cure. Typical uses: General purpose adhesive sea..
Processing Temperature 25.0 °C
77.0 °F
Suggested time at this temperature is 24 hr. May also be cured for shorter time at higher temperatures.
Von Roll Isola IMI E-Solder® 3022 Electrically Conductive Adhesive
Data provided by Von Roll Isola USA.E-SOLDER® epoxy based resin systems can be used at room temperature on heat sensitive materials, can bond dissimilar materials, and do not have flux or residue t..
Processing Temperature 25.0 °C
77.0 °F
Curing time: 16 hours; Postcure: 2 hours/100°C (212°F)
Abatron AboCast 8-3/Abocure 8-3 Epoxy
2-part solvent-free dielectric epoxy casting compound.Processing: 100/50 ratio (pbw); Gel time, 100 g (3.5 oz.): 265 minutes; cures in 16 hours at 25°C (77°F); postcure: 2 hours at 100°C (212°F)..
Processing Temperature 25.0 °C
77.0 °F
Abatron AboCast/AboCure 8109-10
2-part, clear, slow casting/impregnating dielectric compound. Low dielectric constant, good flexibility and thermocycling properties. Abocast 8502-4 is a red (and other colors), filled version.Pro..
Processing Temperature 25.0 °C
77.0 °F
Abatron AboCast/AboCure 8109-11
All-purpose, structural dielectric resin. Better thermal and chemical properties than 8109-8, but requires heat cure. Melts at 70-80°C and remains liquid (supercooled) for many hours at RT.Process..
Processing Temperature 25.0 °C
77.0 °F
Abatron AboCast/AboCure 8109-13
Liquid hardener version of AboCast/AboCure 8109-11.Processing: 100/23 pbw; Potlife: 3-5 h/20°C (68°F), 1-3 h/40°C (105°F), 0.5-1 h/60°C (140°F); mix at RT; cures in: 30 mins/60°C (140°F), 45..