3M Fastbond™ 4224-NF Pressure Sensitive Adhesives

Category Polymer , Adhesive
Manufacturer 3M
Trade Name Fastbond™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M Fastbond™ 4224-NF Pressure Sensitive Adhesives.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
3M™ Fastbond™ Pressure Sensitive Adhesive 4224-NF is a water-based, permanently pressure sensitive adhesive with excellent initial tack and good bond strength.Information provided by 3M
Physical Properties Metric English Comments
Solids Content 39 - 42 %
39 - 42 %
Brookfield Viscosity 9000 - 12000 cP
9000 - 12000 cP
RVF/RVT #6 sp @ 80°F
Mechanical Properties Metric English Comments
Shear Strength 0.0896 MPa
13.0 psi
Neoprene Rubber, 180°, after 48 hrs at 23°C
0.110 MPa
16.0 psi
EPDM, 180°, after 48 hrs at 23°C
0.186 MPa
27.0 psi
Polypropylene, 180°, after 48 hrs at 23°C
0.228 MPa
33.0 psi
HDPE, 180°, after 48 hrs at 23°C
0.276 MPa
40.0 psi
2024 T3 Aluminum, 180°, after 48 hrs at 23°C
0.303 MPa
44.0 psi
Acrylic, 180°, after 48 hrs at 23°C
0.303 MPa
44.0 psi
ABS Plastic, 180°, after 48 hrs at 23°C
0.303 MPa
44.0 psi
Glass, 180°, after 48 hrs at 23°C
0.310 MPa
45.0 psi
Clad Aluminum, 180°, after 48 hrs at 23°C
0.317 MPa
46.0 psi
PVC, 180°, after 48 hrs at 23°C
0.324 MPa
47.0 psi
High Impact Polystyrene, 180°, after 48 hrs at 23°C
0.331 MPa
48.0 psi
Cold Rolled Steel, 180°, after 48 hrs at 23°C
0.331 MPa
48.0 psi
Galvanized Steel, 180°, after 48 hrs at 23°C
0.331 MPa
48.0 psi
Stainless Steel, 180°, after 48 hrs at 23°C
0.345 MPa
50.0 psi
Polycarbonate, 180°, after 48 hrs at 23°C
Peel Strength 0.263 kN/m
1.50 pli
EPDM, 180°, after 48 hrs at 23°C
0.263 kN/m
1.50 pli
HDPE, 180°, after 48 hrs at 23°C
0.280 kN/m
1.60 pli
Neoprene Rubber, 180°, after 48 hrs at 23°C
0.333 kN/m
1.90 pli
Polypropylene, 180°, after 48 hrs at 23°C
0.403 kN/m
2.30 pli
Clad Aluminum, 180°, after 48 hrs at 23°C
0.473 kN/m
2.70 pli
2024 T3 Aluminum, 180°, after 48 hrs at 23°C
0.491 kN/m
2.80 pli
Glass, 180°, after 48 hrs at 23°C
0.508 kN/m
2.90 pli
High Impact Polystyrene, 180°, after 48 hrs at 23°C
0.526 kN/m
3.00 pli
Acrylic, 180°, after 48 hrs at 23°C
0.543 kN/m
3.10 pli
Galvanized Steel, 180°, after 48 hrs at 23°C
0.578 kN/m
3.30 pli
Polycarbonate, 180°, after 48 hrs at 23°C
0.596 kN/m
3.40 pli
PVC, 180°, after 48 hrs at 23°C
0.631 kN/m
3.60 pli
ABS Plastic, 180°, after 48 hrs at 23°C
0.736 kN/m
4.20 pli
Stainless Steel, 180°, after 48 hrs at 23°C
0.771 kN/m
4.40 pli
Cold Rolled Steel, 180°, after 48 hrs at 23°C
Descriptive Properties Value Comments
Appearance Blue, Clear
Base Acrylate